BS 970 (Part 1) 826M31 vs IS 1570 (Part 4) 31Ni10Cr3Mo6

Strong Match — 87.5% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 826M31 (BS 970 (Part 1):1983) and IS 1570 (Part 4) 31Ni10Cr3Mo6 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 826M31 is defined under British Standards (BS), originating from United Kingdom, while IS 1570 (Part 4) 31Ni10Cr3Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 826M31 vs IS 1570 (Part 4) 31Ni10Cr3Mo6 is a 87.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.5%.

Frequently Compared With BS 970 (Part 1) 826M31:
IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 103Cr4
Match Breakdown
CHEMISTRY MATCH
87.5%
MECHANICAL MATCH
No shared data
OVERALL
87.5%
Specifications
Property BS 970 (Part 1) 826M31 IS 1570 (Part 4) 31Ni10Cr3Mo6
Standard BS 970 (Part 1):1983 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) 0.27-0.35 0.27-0.35
Mn (%) 0.45-0.70 0.40-0.70
Cr (%) 0.50-0.80 0.50-0.80
Mo (%) 0.45-0.65 0.40-0.70
Ni (%) 2.30-2.80 2.25-2.75
P (%) <=0.035 Not specified
S (%) <=0.040 Not specified
Si (%) Not specified 0.10-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 826M31 IS 1570 (Part 4) 31Ni10Cr3Mo6
Tensile Strength Not specified 1190-1340 MPa
Yield Strength Not specified >=930 MPa (0.2 % proof stress)
Elongation Not specified >=10%
Izod Impact Not specified >=35 J
Hardness Not specified 341-401 HBS (guidance only)
Condition Not specified Bars and forgings, hardened and tempered (oil hardened unless stated), limiting ruling section 63 mm
Typical Applications
BS 970 (Part 1) 826M31
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
IS 1570 (Part 4) 31Ni10Cr3Mo6
Not documented
Key Differences
Can BS 970 (Part 1) 826M31 Be Substituted With IS 1570 (Part 4) 31Ni10Cr3Mo6?
BS 970 (Part 1) 826M31 and IS 1570 (Part 4) 31Ni10Cr3Mo6 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 4) 31Ni10Cr3Mo6 is often considered as a substitute for BS 970 (Part 1) 826M31 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 826M31
0 active listings and RFQs →
IS 1570 (Part 4) 31Ni10Cr3Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 826M31 and IS 1570 (Part 4) 31Ni10Cr3Mo6?
BS 970 (Part 1) 826M31 specifies P, S which are not specified for IS 1570 (Part 4) 31Ni10Cr3Mo6. IS 1570 (Part 4) 31Ni10Cr3Mo6 specifies Si which is not specified for BS 970 (Part 1) 826M31.
Can BS 970 (Part 1) 826M31 be substituted with IS 1570 (Part 4) 31Ni10Cr3Mo6?
BS 970 (Part 1) 826M31 and IS 1570 (Part 4) 31Ni10Cr3Mo6 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 4) 31Ni10Cr3Mo6 is often considered as a substitute for BS 970 (Part 1) 826M31 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.