Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
Cr
Mo
Ni
P
S
0.12-0.18
0.25-0.50
1.00-1.40
0.15-0.30
3.90-4.30
<=0.035
<=0.040
More data from BS 970 (Part 1):1983
From the standard
Other composition limits
Phosphorus and sulphur
P 0.035 max, S 0.040 max, alloy steels (clause 1.7.2.1)
Residual elements: see clause 1.7.3.
Source: BS 970 (Part 1):1983, clause 1.7.2.1
Mechanical properties, test bar
Test bar diameter (mm)
Rm min (N/mm2)
A min (%)
Izod min (ft lbf)
KCV min (J)
19
1310
8
25
28
Values as printed in Table 11 for the test bar diameter shown. 1 N/mm2 = 1 MPa.
Source: BS 970 (Part 1):1983, Table 11
Heat treatment and maximum hardness
Hardening temperature
800-820 deg C (note 30)
Maximum hardness HB, bars and billets for forging
277
Maximum hardness HB, forgings and bars for machining, sub-critically annealed
277
Maximum hardness HB, forgings and bars for machining, normalized and tempered
269
Maximum hardness values apply when specified on the order, in the condition of delivery. Quantities not limited in Table 12 are not shown. Note 30: shall also be stress relieved at a temperature not exceeding 200 deg C.
Source: BS 970 (Part 1):1983, Table 12
Comparison with earlier editions
BS 970:1970/72 designation
835M15
BS 970:1955 En No.
39B
Appendix D note 47: where a comparison is made the steels are not necessarily equivalent. 'Not listed' means the earlier edition has no entry under this designation.
Source: BS 970 (Part 1):1983, Appendix D