BS 970 (Part 1) 080M15 vs BS 970 (Part 1) 060A40

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 080M15 (BS 970 (Part 1):1991) and BS 970 (Part 1) 060A40 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Carbon Steel category. BS 970 (Part 1) 080M15 is typically used for case hardening steel (section four), while BS 970 (Part 1) 060A40 is commonly used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6.. BS 970 (Part 1) 080M15 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 060A40 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 080M15 vs BS 970 (Part 1) 060A40 is a 86.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With BS 970 (Part 1) 080M15:
BS 970 (Part 1) 080A15 BS 970 (Part 1) 080A15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
86.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property BS 970 (Part 1) 080M15 BS 970 (Part 1) 060A40
Standard BS 970 (Part 1):1991 BS 970 (Part 1):1983
Category Carbon Steel Carbon Steel
C (%) 0.12-0.18 0.38-0.43
Mn (%) 0.60-1.00 0.50-0.70
P (%) Not specified <=0.050
S (%) Not specified <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 080M15 BS 970 (Part 1) 060A40
Condition Case hardened, 19 mm test bar Not specified
Tensile Strength 460 MPa min Not specified
Elongation 18 % min Not specified
Typical Applications
BS 970 (Part 1) 080M15
Case hardening steel (section four)
BS 970 (Part 1) 060A40
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Key Differences
Can BS 970 (Part 1) 080M15 Be Substituted With BS 970 (Part 1) 060A40?
BS 970 (Part 1) 080M15 and BS 970 (Part 1) 060A40 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
BS 970 (Part 1) 080M15
0 active listings and RFQs →
BS 970 (Part 1) 060A40
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 080M15 and BS 970 (Part 1) 060A40?
BS 970 (Part 1) 060A40 specifies P, S which are not specified for BS 970 (Part 1) 080M15.
Can BS 970 (Part 1) 080M15 be substituted with BS 970 (Part 1) 060A40?
BS 970 (Part 1) 080M15 and BS 970 (Part 1) 060A40 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.