BS 970 (Part 1) 303S42 vs IS 1570 (Part 7) 12Cr12MoVH

Minimal Match — 38.9% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 303S42 (BS 970 (Part 1):1991) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 303S42 is typically used for austenitic stainless and heat resisting steel (section five), while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. BS 970 (Part 1) 303S42 is defined under British Standards (BS), originating from United Kingdom, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 303S42 vs IS 1570 (Part 7) 12Cr12MoVH is a 58.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 38.9%.

Frequently Compared With BS 970 (Part 1) 303S42:
ASTM A959 16-8-2H EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
58.3%
MECHANICAL MATCH
0%
OVERALL
38.9%
Specifications
Property BS 970 (Part 1) 303S42 IS 1570 (Part 7) 12Cr12MoVH
Standard BS 970 (Part 1):1991 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.12 0.08-0.16
Si (%) <=1.0 <=0.60
Mn (%) <=2.0 0.40-1.00
P (%) <=0.060 <=0.040
S (%) <=0.060 <=0.035
Cr (%) 17.0-19.0 11.5-13.00
Mo (%) <=1.00 0.40-0.80
Ni (%) 8.0-10.0 <=1.0
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 303S42 IS 1570 (Part 7) 12Cr12MoVH
Condition Softened, 1000-1100 deg C Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Tensile Strength 510 MPa min 770-930 MPa
Yield Strength 190 MPa min (0.2% proof) >=585 MPa (0.2 % proof stress)
Elongation 40 % min >=15%
Hardness 183 HB max Not specified
Typical Applications
BS 970 (Part 1) 303S42
Austenitic stainless and heat resisting steel (section five)
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can BS 970 (Part 1) 303S42 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
BS 970 (Part 1) 303S42 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
BS 970 (Part 1) 303S42
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 303S42 and IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 7) 12Cr12MoVH specifies V which is not specified for BS 970 (Part 1) 303S42.
Can BS 970 (Part 1) 303S42 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
BS 970 (Part 1) 303S42 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.