BS 970 (Part 1) 304S11 vs EN 10088-1 X2CrNiN18-10

Strong Match — 87.3% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 304S11 (BS 970 (Part 1):1991) and EN 10088-1 X2CrNiN18-10 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 304S11 is defined under British Standards (BS), originating from United Kingdom, while EN 10088-1 X2CrNiN18-10 is defined under European Standard (EN), originating from Europe.

As per chemical composition, BS 970 (Part 1) 304S11 vs EN 10088-1 X2CrNiN18-10 is a 87.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.3%.

Frequently Compared With BS 970 (Part 1) 304S11:
EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 201L ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
87.3%
MECHANICAL MATCH
No shared data
OVERALL
87.3%
Specifications
Property BS 970 (Part 1) 304S11 EN 10088-1 X2CrNiN18-10
Standard BS 970 (Part 1):1991 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Cr (%) 17.0-19.0 17.5-19.5
Ni (%) 9.0-12.0 8.5-11.5
N (%) Not specified 0.12-0.22
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 304S11 EN 10088-1 X2CrNiN18-10
Condition Softened, 1000-1100 deg C Not specified
Tensile Strength 480 MPa min Not specified
Yield Strength 180 MPa min (0.2% proof) Not specified
Elongation 40 % min Not specified
Hardness 183 HB max Not specified
Typical Applications
BS 970 (Part 1) 304S11
Austenitic stainless and heat resisting steel (section five)
EN 10088-1 X2CrNiN18-10
Not documented
Key Differences
Can BS 970 (Part 1) 304S11 Be Substituted With EN 10088-1 X2CrNiN18-10?
BS 970 (Part 1) 304S11 and EN 10088-1 X2CrNiN18-10 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiN18-10 is often considered as a substitute for BS 970 (Part 1) 304S11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 304S11
0 active listings and RFQs →
EN 10088-1 X2CrNiN18-10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 304S11 and EN 10088-1 X2CrNiN18-10?
EN 10088-1 X2CrNiN18-10 specifies N which is not specified for BS 970 (Part 1) 304S11.
Can BS 970 (Part 1) 304S11 be substituted with EN 10088-1 X2CrNiN18-10?
BS 970 (Part 1) 304S11 and EN 10088-1 X2CrNiN18-10 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiN18-10 is often considered as a substitute for BS 970 (Part 1) 304S11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.