Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
BS 970 (Part 1) 316S11 (BS 970 (Part 1):1991) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
BS 970 (Part 1) 316S11 is typically used for austenitic stainless and heat resisting steel (section five), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
BS 970 (Part 1) 316S11 is defined under British Standards (BS), originating from United Kingdom, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, BS 970 (Part 1) 316S11 vs EN 10088-1 1.4845 is a 59.6% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
BS 970 (Part 1) 316S11
EN 10088-1 1.4845
Condition
Softened, 1000-1100 deg C
Not specified
Tensile Strength
490 MPa min
≥515 MPa
Yield Strength
190 MPa min (0.2% proof)
≥205 MPa
Elongation
40 % min
≥40%
Hardness
183 HB max
Not specified
Max Service Temp
Not specified
1100°C continuous
Typical Applications
BS 970 (Part 1) 316S11
Austenitic stainless and heat resisting steel (section five)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
BS 970 (Part 1) 316S11 specifies P, S, Mo which are not specified for EN 10088-1 1.4845.
Can BS 970 (Part 1) 316S11 Be Substituted With EN 10088-1 1.4845?
BS 970 (Part 1) 316S11 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between BS 970 (Part 1) 316S11 and EN 10088-1 1.4845?
BS 970 (Part 1) 316S11 specifies P, S, Mo which are not specified for EN 10088-1 1.4845.
Can BS 970 (Part 1) 316S11 be substituted with EN 10088-1 1.4845?
BS 970 (Part 1) 316S11 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.