BS 970 (Part 1) 416S29 vs IS 1570 (Part 7) 12Cr13H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 416S29 (BS 970 (Part 1):1991) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 416S29 is typically used for ferritic and martensitic stainless and heat resisting steel (section five), while IS 1570 (Part 7) 12Cr13H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. BS 970 (Part 1) 416S29 is defined under British Standards (BS), originating from United Kingdom, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 416S29 vs IS 1570 (Part 7) 12Cr13H is a 77.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 (Part 1) 416S29:
IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
77.6%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property BS 970 (Part 1) 416S29 IS 1570 (Part 7) 12Cr13H
Standard BS 970 (Part 1):1991 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.14-0.20 0.09-0.15
Si (%) <=1.0 <=1.00
Mn (%) <=1.5 <=1.00
P (%) <=0.060 <=0.040
S (%) 0.15-0.35 <=0.030
Cr (%) 11.5-13.5 11.5-14.00
Mo (%) <=0.60 Not specified
Ni (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 416S29 IS 1570 (Part 7) 12Cr13H
Tensile Strength Not specified 470-670 MPa
Yield Strength Not specified >=265 MPa (0.2 % proof stress)
Elongation Not specified >=20%
Condition Not specified Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Typical Applications
BS 970 (Part 1) 416S29
Ferritic and martensitic stainless and heat resisting steel (section five)
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can BS 970 (Part 1) 416S29 Be Substituted With IS 1570 (Part 7) 12Cr13H?
BS 970 (Part 1) 416S29 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
BS 970 (Part 1) 416S29
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr13H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 416S29 and IS 1570 (Part 7) 12Cr13H?
BS 970 (Part 1) 416S29 specifies Mo which is not specified for IS 1570 (Part 7) 12Cr13H.
Can BS 970 (Part 1) 416S29 be substituted with IS 1570 (Part 7) 12Cr13H?
BS 970 (Part 1) 416S29 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.