BS 970 (Part 1) 635M15 vs BS 970 (Part 3) 635M15

Strong Match — 93.7% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 635M15 (BS 970 (Part 1):1991) and BS 970 (Part 3) 635M15 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 635M15 is typically used for case hardening steel (section four), while BS 970 (Part 3) 635M15 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (table 15). BS 970 (Part 1) 635M15 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 3) 635M15 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 635M15 vs BS 970 (Part 3) 635M15 is a 93.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.7%.

Frequently Compared With BS 970 (Part 1) 635M15:
IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4
Match Breakdown
CHEMISTRY MATCH
93.7%
MECHANICAL MATCH
No shared data
OVERALL
93.7%
Specifications
Property BS 970 (Part 1) 635M15 BS 970 (Part 3) 635M15
Standard BS 970 (Part 1):1991 BS 970 (Part 3):1991
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.12-0.18
Mn (%) 0.60-0.90 0.60-0.90
Cr (%) 0.40-0.80 0.4-0.80
Ni (%) 0.70-1.10 0.70-1.10
Si (%) Not specified 0.10-0.40
P (%) Not specified <=0.04
S (%) Not specified <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 635M15 BS 970 (Part 3) 635M15
Condition Case hardened, 19 mm test bar Not specified
Tensile Strength 770 MPa min Not specified
Elongation 12 % min Not specified
Typical Applications
BS 970 (Part 1) 635M15
Case hardening steel (section four)
BS 970 (Part 3) 635M15
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (Table 15)
Key Differences
Can BS 970 (Part 1) 635M15 Be Substituted With BS 970 (Part 3) 635M15?
BS 970 (Part 1) 635M15 and BS 970 (Part 3) 635M15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 635M15 is often considered as a substitute for BS 970 (Part 1) 635M15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 635M15
0 active listings and RFQs →
BS 970 (Part 3) 635M15
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 635M15 and BS 970 (Part 3) 635M15?
BS 970 (Part 3) 635M15 specifies Si, P, S which are not specified for BS 970 (Part 1) 635M15.
Can BS 970 (Part 1) 635M15 be substituted with BS 970 (Part 3) 635M15?
BS 970 (Part 1) 635M15 and BS 970 (Part 3) 635M15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 635M15 is often considered as a substitute for BS 970 (Part 1) 635M15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.