BS 970 (Part 1) 805M17 vs BS 970 (Part 1) 805A17

Strong Match — 94.1% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 805M17 (BS 970 (Part 1):1991) and BS 970 (Part 1) 805A17 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 805M17 is typically used for case hardening steel (section four), while BS 970 (Part 1) 805A17 is commonly used for case hardening steel (section four). BS 970 (Part 1) 805M17 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 805A17 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 805M17 vs BS 970 (Part 1) 805A17 is a 91.1% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 94.1%.

Frequently Compared With BS 970 (Part 1) 805M17:
IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 10Cr20Mo6
Match Breakdown
CHEMISTRY MATCH
91.1%
MECHANICAL MATCH
100%
OVERALL
94.1%
Specifications
Property BS 970 (Part 1) 805M17 BS 970 (Part 1) 805A17
Standard BS 970 (Part 1):1991 BS 970 (Part 1):1991
Category Alloy Steel Alloy Steel
C (%) 0.14-0.20 0.15-0.20
Mn (%) 0.60-0.95 0.70-0.90
Cr (%) 0.35-0.65 0.40-0.60
Mo (%) 0.15-0.25 0.15-0.25
Ni (%) 0.35-0.75 0.40-0.70
P (%) <=0.035 <=0.035
S (%) <=0.035 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 805M17 BS 970 (Part 1) 805A17
Condition Case hardened, 19 mm test bar Case hardened, 19 mm test bar
Tensile Strength 770 MPa min 770 MPa min
Elongation 12 % min 12 % min
Typical Applications
BS 970 (Part 1) 805M17
Case hardening steel (section four)
BS 970 (Part 1) 805A17
Case hardening steel (section four)
Can BS 970 (Part 1) 805M17 Be Substituted With BS 970 (Part 1) 805A17?
BS 970 (Part 1) 805M17 and BS 970 (Part 1) 805A17 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 805A17 is often considered as a substitute for BS 970 (Part 1) 805M17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 805M17
0 active listings and RFQs →
BS 970 (Part 1) 805A17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 805M17 and BS 970 (Part 1) 805A17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 805M17 be substituted with BS 970 (Part 1) 805A17?
BS 970 (Part 1) 805M17 and BS 970 (Part 1) 805A17 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 805A17 is often considered as a substitute for BS 970 (Part 1) 805M17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.