BS 970 (Part 1) 822H17 vs IS 4367 16Ni8Cr6Mo2

Strong Match — 86.6% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 822H17 (BS 970 (Part 1):1991) and IS 4367 16Ni8Cr6Mo2 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 822H17 is typically used for case hardening steel (section four), while IS 4367 16Ni8Cr6Mo2 is commonly used for gears, camshafts, piston pins, splined shafts, aerospace and automotive case-hardened components.. BS 970 (Part 1) 822H17 is defined under British Standards (BS), originating from United Kingdom, while IS 4367 16Ni8Cr6Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 822H17 vs IS 4367 16Ni8Cr6Mo2 is a 86.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.6%.

Frequently Compared With BS 970 (Part 1) 822H17:
IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
86.6%
MECHANICAL MATCH
No shared data
OVERALL
86.6%
Specifications
Property BS 970 (Part 1) 822H17 IS 4367 16Ni8Cr6Mo2
Standard BS 970 (Part 1):1991 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.14-0.20 0.12-0.20
Mn (%) 0.40-0.70 0.40-0.70
Cr (%) 1.30-1.70 1.40-1.70
Mo (%) 0.15-0.25 0.15-0.25
Ni (%) 1.75-2.25 1.80-2.20
Si (%) Not specified 0.10-0.35
S (%) Not specified <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 822H17 IS 4367 16Ni8Cr6Mo2
Tensile Strength Not specified 1350 MPa min
Elongation Not specified >=9%
Izod Impact Not specified 35 J min
Hardness (soft annealed) Not specified <=229 HB
Condition Not specified Refined, quenched and stress relieved (core properties), ruling section up to 30 mm
Typical Applications
BS 970 (Part 1) 822H17
Case hardening steel (section four)
IS 4367 16Ni8Cr6Mo2
Gears, camshafts, piston pins, splined shafts, aerospace and automotive case-hardened components.
Key Differences
Can BS 970 (Part 1) 822H17 Be Substituted With IS 4367 16Ni8Cr6Mo2?
BS 970 (Part 1) 822H17 and IS 4367 16Ni8Cr6Mo2 overlap closely enough on chemistry and mechanical properties that IS 4367 16Ni8Cr6Mo2 is often considered as a substitute for BS 970 (Part 1) 822H17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
BS 970 (Part 1) 822H17
No active listings currently.
IS 4367 16Ni8Cr6Mo2
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5200–6300 mm (204.72–248.03 in)
On M-EX Right Now
BS 970 (Part 1) 822H17
0 active listings and RFQs →
IS 4367 16Ni8Cr6Mo2
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 822H17 and IS 4367 16Ni8Cr6Mo2?
IS 4367 16Ni8Cr6Mo2 specifies Si, S, P which are not specified for BS 970 (Part 1) 822H17.
Can BS 970 (Part 1) 822H17 be substituted with IS 4367 16Ni8Cr6Mo2?
BS 970 (Part 1) 822H17 and IS 4367 16Ni8Cr6Mo2 overlap closely enough on chemistry and mechanical properties that IS 4367 16Ni8Cr6Mo2 is often considered as a substitute for BS 970 (Part 1) 822H17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.