Close Alternative — 75.7% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 832M13 (BS 970 (Part 1):1991) and EN 10084 14NiCrMo13-4 (EN 10084:2008) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 832M13 is typically used for case hardening steel (section four), while EN 10084 14NiCrMo13-4 is commonly used for case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1). BS 970 (Part 1) 832M13 is defined under British Standards (BS), originating from United Kingdom, while EN 10084 14NiCrMo13-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, BS 970 (Part 1) 832M13 vs EN 10084 14NiCrMo13-4 is a 75.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 75.7%.

Frequently Compared With BS 970 (Part 1) 832M13:
IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 UNI 11234 100Cr6
Match Breakdown
CHEMISTRY MATCH
75.7%
MECHANICAL MATCH
No shared data
OVERALL
75.7%
Specifications
Property BS 970 (Part 1) 832M13 EN 10084 14NiCrMo13-4
Standard BS 970 (Part 1):1991 EN 10084:2008
Category Alloy Steel Alloy Steel
C (%) 0.10-0.16 0.11-0.17
Mn (%) 0.35-0.60 0.30-0.60
Cr (%) 0.70-1.00 0.80-1.10
Mo (%) 0.10-0.25 0.20-0.30
Ni (%) 3.00-3.75 3.00-3.50
P (%) Not specified <=0.025
S (%) Not specified <=0.035
Si (%) Not specified <=0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 832M13 EN 10084 14NiCrMo13-4
Condition Case hardened, 19 mm test bar Soft annealed
Tensile Strength 1080 MPa min Not specified
Elongation 8 % min Not specified
Hardenability Not specified +H band at 1.5 mm from the quenched end: 39 to 47 HRC
Hardness Not specified Soft annealed: 241 HB max
Typical Applications
BS 970 (Part 1) 832M13
Case hardening steel (section four)
EN 10084 14NiCrMo13-4
Case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1)
Key Differences
Can BS 970 (Part 1) 832M13 Be Substituted With EN 10084 14NiCrMo13-4?
BS 970 (Part 1) 832M13 and EN 10084 14NiCrMo13-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
BS 970 (Part 1) 832M13
0 active listings and RFQs →
EN 10084 14NiCrMo13-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 832M13 and EN 10084 14NiCrMo13-4?
EN 10084 14NiCrMo13-4 specifies P, S, Si which are not specified for BS 970 (Part 1) 832M13.
Can BS 970 (Part 1) 832M13 be substituted with EN 10084 14NiCrMo13-4?
BS 970 (Part 1) 832M13 and EN 10084 14NiCrMo13-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.