Bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. Suitable for tensile ranges 55/65 (T) and 65/75 (V) tons/sq in; purchaser to state T or V on the order.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
Cr
S
P
0.50-0.70
0.10-0.35
0.50-0.80
0.50-0.80
<=0.050
<=0.050
Mechanical Properties
Tensile Strength
≥849 MPa (55 tons/sq in, converted)
Yield Strength
≥618 MPa (40 tons/sq in, converted)
Elongation
≥15%
Hardness
248-302 HB
Condition
Hardened and tempered T, ruling section 2 1/2 in (lowest-strength condition of the standard)
More data from BS 970:1955
From the standard
Condition of material on delivery
A
Bars and billets for forging as rolled or forged unless order states otherwise.
B
Forgings and drop-forgings finally heat treated unless order states otherwise.
C
Bars for machining finally heat treated unless order states otherwise.
D
Bright bars finally heat treated, before or after cold work at manufacturer option, unless order states otherwise.
Source: BS 970:1955, Part 2, En 11 (page 64)
Mechanical properties
Condition
Ruling section or size (in)
Tensile strength (tons/sq in)
Yield stress (tons/sq in)
Elongation (%)
Izod impact (ft lb)
Brinell (HB)
Proof stress 0.2% (tons/sq in), when requested
Hardened and tempered T
2 1/2
55
40
15
25
248-302
-
Hardened and tempered V
2 1/2
65
48
12
12
293-341
-
Values as printed in BS 970:1955; tensile strength, yield stress and proof stress in tons/sq in, Izod in ft lb. Minimum unless a range is shown.
Source: BS 970:1955, Part 2, En 11 (page 65)
Heat treatment
Harden (oil)
800/850 C
Temper
suitable temperature between 500 C and 700 C
Temperatures in degrees C as printed.
Source: BS 970:1955, Part 2, En 11 (page 64)
Status in the 1955 edition
Status
Deleted by Amendment 7
Reason
Amendment 7 (Sep 1970): direct hardening alloy steels moved to BS 970 Part 2:1970
BS 970:1955 was amended up to Amendment 10 (June 1972); steels were moved to the revised Parts 1 to 5 and deleted from this edition.
Source: BS 970:1955, Amendment slips 6 to 10