BS 970 EN110 vs BS 970 (Part 1) 815H17

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

BS 970 EN110 (BS 970:1955) and BS 970 (Part 1) 815H17 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 EN110 is typically used for bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. suitable for 50/60 (s), 55/65 (t), 60/70 (u), 65/75 (v), 70/80 (w) tons/sq in according to ruling section. capable of meeting the test requirements of en 16, en 17 and en 19., while BS 970 (Part 1) 815H17 is commonly used for case hardening steel (section four). BS 970 EN110 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 815H17 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 EN110 vs BS 970 (Part 1) 815H17 is a 74% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With BS 970 EN110:
IS 1570 (Part 4) 07Cr4Mo6 IS 4367 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 UNI 11234 100Cr6 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
74%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property BS 970 EN110 BS 970 (Part 1) 815H17
Standard BS 970:1955 BS 970 (Part 1):1991
Category Alloy Steel Alloy Steel
C (%) 0.35-0.45 0.14-0.20
Si (%) 0.10-0.35 Not specified
Mn (%) 0.40-0.80 0.80-0.90
Ni (%) 1.20-1.60 1.20-1.70
Cr (%) 0.90-1.40 0.80-1.20
Mo (%) 0.10-0.20 0.10-0.20
S (%) <=0.050 Not specified
P (%) <=0.050 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN110 BS 970 (Part 1) 815H17
Tensile Strength ≥772 MPa (50 tons/sq in, converted) Not specified
Yield Strength ≥587 MPa (38 tons/sq in, converted) Not specified
Elongation ≥20% Not specified
Hardness 223-277 HB Not specified
Condition Hardened and tempered S, ruling section 6 in (lowest-strength condition of the standard) Not specified
Typical Applications
BS 970 EN110
Bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. Suitable for 50/60 (S), 55/65 (T), 60/70 (U), 65/75 (V), 70/80 (W) tons/sq in according to ruling section. Capable of meeting the test requirements of En 16, En 17 and En 19.
BS 970 (Part 1) 815H17
Case hardening steel (section four)
Key Differences
Can BS 970 EN110 Be Substituted With BS 970 (Part 1) 815H17?
BS 970 EN110 and BS 970 (Part 1) 815H17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
BS 970 EN110
0 active listings and RFQs →
BS 970 (Part 1) 815H17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN110 and BS 970 (Part 1) 815H17?
BS 970 EN110 specifies Si, S, P which are not specified for BS 970 (Part 1) 815H17.
Can BS 970 EN110 be substituted with BS 970 (Part 1) 815H17?
BS 970 EN110 and BS 970 (Part 1) 815H17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.