BS 970 EN14B vs IS 1570 (Part 4) 103Cr4

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 EN14B (BS 970:1955) and IS 1570 (Part 4) 103Cr4 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. BS 970 EN14B is defined under British Standards (BS), originating from United Kingdom, while IS 1570 (Part 4) 103Cr4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 EN14B vs IS 1570 (Part 4) 103Cr4 is a 68.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 EN14B:
IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4
Match Breakdown
CHEMISTRY MATCH
68.7%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property BS 970 EN14B IS 1570 (Part 4) 103Cr4
Standard BS 970:1955 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) 0.20-0.30 0.95-1.10
Si (%) 0.10-0.35 0.10-0.35
Mn (%) 1.30-1.70 0.25-0.45
Ni (%) <=0.40 Not specified
S (%) <=0.060 Not specified
P (%) <=0.060 Not specified
Cr (%) Not specified 0.90-1.20
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN14B IS 1570 (Part 4) 103Cr4
Tensile Strength ≥510 MPa (33 tons/sq in, converted) Not specified
Yield Strength ≥355 MPa (23 tons/sq in, converted) Not specified
Elongation ≥20% Not specified
Hardness 170-223 HB Not specified
Condition Normalised, ruling section 5 in (lowest-strength condition of the standard) Not specified
Typical Applications
BS 970 EN14B
Bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. Suitable hardened and tempered for 40/50 (Q) and 45/55 (R) tons/sq in according to ruling section.
IS 1570 (Part 4) 103Cr4
Not documented
Key Differences
Can BS 970 EN14B Be Substituted With IS 1570 (Part 4) 103Cr4?
BS 970 EN14B and IS 1570 (Part 4) 103Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
BS 970 EN14B
0 active listings and RFQs →
IS 1570 (Part 4) 103Cr4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN14B and IS 1570 (Part 4) 103Cr4?
BS 970 EN14B specifies Ni, S, P which are not specified for IS 1570 (Part 4) 103Cr4. IS 1570 (Part 4) 103Cr4 specifies Cr which is not specified for BS 970 EN14B.
Can BS 970 EN14B be substituted with IS 1570 (Part 4) 103Cr4?
BS 970 EN14B and IS 1570 (Part 4) 103Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.