Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
S
P
0.30-0.40
<=0.25
1.30-1.70
0.12-0.20
<=0.060
Mechanical Properties
Tensile Strength
≥695 MPa (45 tons/sq in, converted)
Yield Strength
≥525 MPa (34 tons/sq in, converted)
Elongation
≥20%
Hardness
201-255 HB
Condition
Hardened and tempered R, ruling section 2 1/2 in (lowest-strength condition of the standard)
More data from BS 970:1955
From the standard
Condition of material on delivery
A
Bars and billets for forging as rolled or forged unless order states otherwise.
B
Forgings and drop-forgings finally heat treated unless order states otherwise.
C
Bars for machining finally heat treated unless order states otherwise.
D
Bright bars finally heat treated, before or after cold work at manufacturer option, unless order states otherwise.
Source: BS 970:1955, Part 2, En 15AM (page 80)
Mechanical properties
Condition
Ruling section or size (in)
Tensile strength (tons/sq in)
Yield stress (tons/sq in)
Elongation (%)
Izod impact (ft lb)
Brinell (HB)
Proof stress 0.2% (tons/sq in), when requested
Hardened and tempered R
2 1/2
45
34
20
25
201-255
-
Values as printed in BS 970:1955; tensile strength, yield stress and proof stress in tons/sq in, Izod in ft lb. Minimum unless a range is shown.
Source: BS 970:1955, Part 2, En 15AM (page 81)
Heat treatment
Harden (oil)
840/870 C
Temper
suitable temperature between 550 C and 660 C
Temperatures in degrees C as printed.
Source: BS 970:1955, Part 2, En 15AM (page 80)
Status in the 1955 edition
Status
Deleted by Amendment 9
Reason
Amendment 9 (Feb 1972): carbon and carbon-manganese steels moved to BS 970 Part 1:1972
BS 970:1955 was amended up to Amendment 10 (June 1972); steels were moved to the revised Parts 1 to 5 and deleted from this edition.
Source: BS 970:1955, Amendment slips 6 to 10