BS 970 EN1A Leaded vs BS 970 (Part 1) 210A15

Close Alternative — 80.6% match based on chemical composition and mechanical property overlap.

BS 970 EN1A Leaded (BS 970:1955) and BS 970 (Part 1) 210A15 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Free Machining Steel category. BS 970 EN1A Leaded is typically used for high speed automatic machining, precision parts, while BS 970 (Part 1) 210A15 is commonly used for case hardening steel for mechanical and allied engineering purposes (table 11 mechanical properties).. BS 970 EN1A Leaded is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 210A15 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 EN1A Leaded vs BS 970 (Part 1) 210A15 is a 80.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 80.6%.

Frequently Compared With BS 970 EN1A Leaded:
SAE J403 1117 SAE J403 1117 SAE J403 1118 SAE J403 1126 SAE J403 1117 SAE J403 1118 SAE J403 1126 IS 1570 (Part 3) 10C8S10 IS 4432 10C8S10 SAE J403 1126 SAE J403 1118 SAE J403 1132
Match Breakdown
CHEMISTRY MATCH
80.6%
MECHANICAL MATCH
No shared data
OVERALL
80.6%
Specifications
Property BS 970 EN1A Leaded BS 970 (Part 1) 210A15
Standard BS 970:1955 BS 970 (Part 1):1983
Category Free Machining Steel Free Machining Steel
C (%) 0.07–0.15 0.13-0.18
Mn (%) 0.80–1.20 0.90-1.20
S (%) 0.20–0.30 0.10-0.18
Pb (%) 0.15–0.35 Not specified
P (%) Not specified <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN1A Leaded BS 970 (Part 1) 210A15
Tensile Strength 380–490 MPa Not specified
Elongation ≥20% Not specified
Hardness ≤152 HB Not specified
Typical Applications
BS 970 EN1A Leaded
High speed automatic machining, precision parts
BS 970 (Part 1) 210A15
Case hardening steel for mechanical and allied engineering purposes (Table 11 mechanical properties).
Key Differences
Can BS 970 EN1A Leaded Be Substituted With BS 970 (Part 1) 210A15?
BS 970 EN1A Leaded and BS 970 (Part 1) 210A15 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
BS 970 EN1A Leaded
Round Bar → (3 listings)
Diameter: 30–30 mm (1.18–1.18 in)
Length: 2700–3800 mm (106.3–149.61 in)
BS 970 (Part 1) 210A15
No active listings currently.
On M-EX Right Now
BS 970 EN1A Leaded
3 active listings and RFQs →
BS 970 (Part 1) 210A15
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN1A Leaded and BS 970 (Part 1) 210A15?
BS 970 EN1A Leaded specifies Pb which is not specified for BS 970 (Part 1) 210A15. BS 970 (Part 1) 210A15 specifies P which is not specified for BS 970 EN1A Leaded.
Can BS 970 EN1A Leaded be substituted with BS 970 (Part 1) 210A15?
BS 970 EN1A Leaded and BS 970 (Part 1) 210A15 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.