BS 970 EN2C vs BS 970 (Part 1) 045A10

Strong Match — 89.5% match based on chemical composition and mechanical property overlap.

BS 970 EN2C (BS 970:1955) and BS 970 (Part 1) 045A10 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. BS 970 EN2C is typically used for bars and billets for forging; forgings and drop-forgings; bars for machining, while BS 970 (Part 1) 045A10 is commonly used for case hardening steel (section four). BS 970 EN2C is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 045A10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 EN2C vs BS 970 (Part 1) 045A10 is a 89.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.5%.

Frequently Compared With BS 970 EN2C:
BS 970 (Part 1) 055M15 BS 970 (Part 1) 070M20 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045A10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 060A40 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10
Match Breakdown
CHEMISTRY MATCH
89.5%
MECHANICAL MATCH
No shared data
OVERALL
89.5%
Specifications
Property BS 970 EN2C BS 970 (Part 1) 045A10
Standard BS 970:1955 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.15-0.25 0.08-0.13
Mn (%) 0.40-0.60 0.30-0.60
S (%) <=0.050 Not specified
P (%) <=0.050 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN2C BS 970 (Part 1) 045A10
Condition Not specified Case hardened, 19 mm test bar
Tensile Strength Not specified 430 MPa min
Elongation Not specified 18 % min
Typical Applications
BS 970 EN2C
Bars and billets for forging; forgings and drop-forgings; bars for machining
BS 970 (Part 1) 045A10
Case hardening steel (section four)
Key Differences
Can BS 970 EN2C Be Substituted With BS 970 (Part 1) 045A10?
BS 970 EN2C and BS 970 (Part 1) 045A10 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 045A10 is often considered as a substitute for BS 970 EN2C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 EN2C
0 active listings and RFQs →
BS 970 (Part 1) 045A10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN2C and BS 970 (Part 1) 045A10?
BS 970 EN2C specifies S, P which are not specified for BS 970 (Part 1) 045A10.
Can BS 970 EN2C be substituted with BS 970 (Part 1) 045A10?
BS 970 EN2C and BS 970 (Part 1) 045A10 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 045A10 is often considered as a substitute for BS 970 EN2C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.