BS 970 EN2D vs IS 11169 (Part 1) 14C6

Strong Match — 92.7% match based on chemical composition and mechanical property overlap.

BS 970 EN2D (BS 970:1955) and IS 11169 (Part 1) 14C6 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Carbon Steel category. BS 970 EN2D is typically used for bars and billets for forging; forgings and drop-forgings; bars for machining, while IS 11169 (Part 1) 14C6 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). BS 970 EN2D is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 1) 14C6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 EN2D vs IS 11169 (Part 1) 14C6 is a 92.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.7%.

Frequently Compared With BS 970 EN2D:
BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 060A40
Match Breakdown
CHEMISTRY MATCH
92.7%
MECHANICAL MATCH
No shared data
OVERALL
92.7%
Specifications
Property BS 970 EN2D IS 11169 (Part 1) 14C6
Standard BS 970:1955 IS 11169 (Part 1):1984
Category Carbon Steel Carbon Steel
C (%) 0.15-0.30 0.10-0.18
Mn (%) 0.40-0.70 0.40-0.70
S (%) <=0.050 Not specified
P (%) <=0.050 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN2D IS 11169 (Part 1) 14C6
Core Tensile Strength Not specified >=500 MPa (Over 15 up to 30 mm)
Core Elongation Not specified >=17% (Over 15 up to 30 mm)
Hardness, annealed Not specified <=140 HB
Typical Applications
BS 970 EN2D
Bars and billets for forging; forgings and drop-forgings; bars for machining
IS 11169 (Part 1) 14C6
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Key Differences
Can BS 970 EN2D Be Substituted With IS 11169 (Part 1) 14C6?
BS 970 EN2D and IS 11169 (Part 1) 14C6 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 14C6 is often considered as a substitute for BS 970 EN2D in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 EN2D
0 active listings and RFQs →
IS 11169 (Part 1) 14C6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN2D and IS 11169 (Part 1) 14C6?
BS 970 EN2D specifies S, P which are not specified for IS 11169 (Part 1) 14C6.
Can BS 970 EN2D be substituted with IS 11169 (Part 1) 14C6?
BS 970 EN2D and IS 11169 (Part 1) 14C6 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 14C6 is often considered as a substitute for BS 970 EN2D in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.