BS 970 EN32B vs BS 970 (Part 1) 040A10

Close Alternative — 81.8% match based on chemical composition and mechanical property overlap.

BS 970 EN32B (BS 970:1955) and BS 970 (Part 1) 040A10 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. BS 970 EN32B is typically used for bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. recommended for limiting ruling sections over 1/2 in. en 32c same title., while BS 970 (Part 1) 040A10 is commonly used for used for bolts, studs, shafts, brackets, fabricated components, and general engineering parts.. BS 970 EN32B is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 040A10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 EN32B vs BS 970 (Part 1) 040A10 is a 81.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 81.8%.

Frequently Compared With BS 970 EN32B:
BS 970 (Part 3) 080A15 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A40 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
81.8%
MECHANICAL MATCH
No shared data
OVERALL
81.8%
Specifications
Property BS 970 EN32B BS 970 (Part 1) 040A10
Standard BS 970:1955 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.10-0.18 0.08-0.13
Si (%) 0.05-0.35 Not specified
Mn (%) 0.60-1.00 0.30-0.50
S (%) <=0.070 Not specified
P (%) <=0.050 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN32B BS 970 (Part 1) 040A10
Tensile Strength ≥494 MPa (32 tons/sq in, converted) Not specified
Elongation ≥20% Not specified
Condition Core, after heat treatment (lowest-strength condition of the standard) Not specified
Typical Applications
BS 970 EN32B
Bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. Recommended for limiting ruling sections over 1/2 in. En 32C same title.
BS 970 (Part 1) 040A10
Used for bolts, studs, shafts, brackets, fabricated components, and general engineering parts.
Key Differences
Can BS 970 EN32B Be Substituted With BS 970 (Part 1) 040A10?
BS 970 EN32B and BS 970 (Part 1) 040A10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
BS 970 EN32B
No active listings currently.
BS 970 (Part 1) 040A10
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4700–5500 mm (185.04–216.54 in)
On M-EX Right Now
BS 970 EN32B
0 active listings and RFQs →
BS 970 (Part 1) 040A10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN32B and BS 970 (Part 1) 040A10?
BS 970 EN32B specifies Si, S, P which are not specified for BS 970 (Part 1) 040A10.
Can BS 970 EN32B be substituted with BS 970 (Part 1) 040A10?
BS 970 EN32B and BS 970 (Part 1) 040A10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.