Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
Ni
Mo
S
P
0.20-0.25
0.10-0.35
0.30-0.60
1.50-2.00
0.20-0.30
<=0.050
<=0.050
More data from BS 970:1955
From the standard
Condition of material on delivery
A
Bars and billets for forging as rolled or forged unless order states otherwise.
B
Forgings and drop-forgings as forged unless order states otherwise.
C
Bars for machining as rolled unless order states otherwise.
D
Bright bars in the cold worked condition suitable for machining unless order states otherwise; maximum Brinell hardness may be agreed between purchaser and manufacturer.
Source: BS 970:1955, Part 2, En 35A (page 126)
Heat treatment
Blank carburise (1 1/8 in diameter test bars)
880/930 C
Refine (1 1/8 in diameter test bars)
850/880 C, cool in air, oil or water
Harden (oil) (1 1/8 in diameter test bars)
760/780 C
Temperatures in degrees C as printed.
Source: BS 970:1955, Part 2, En 35A (page 126)
Notes
Note
See Appendix A for single quench treatment. By arrangement with the purchaser tests may be carried out on samples from which blank carburising has been omitted or modified to a short heating period.
Source: BS 970:1955, Part 2, En 35A
Status in the 1955 edition
Status
Deleted by Amendment 8
Reason
Amendment 8 (Jul 1971): alloy case hardening steels moved to BS 970 Part 3:1971
BS 970:1955 was amended up to Amendment 10 (June 1972); steels were moved to the revised Parts 1 to 5 and deleted from this edition.
Source: BS 970:1955, Amendment slips 6 to 10