Bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. Suitable for tensile strength 65 tons/sq in min. Supplied on tensile strength only or, by special arrangement, on analysis only.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
Ni
Cr
Mo
S
P
0.22-0.26
<=0.35
0.70-1.00
0.40-0.70
0.55-0.80
0.08-0.15
<=0.050
<=0.050
Mechanical Properties
Tensile Strength
≥1004 MPa (65 tons/sq in, converted)
Condition
min (lowest-strength condition of the standard)
More data from BS 970:1955
From the standard
Condition of material on delivery
A
Bars and billets for forging as rolled or forged.
B
Forgings and drop-forgings as forged.
C
Bars for machining as rolled.
D
Bright bars cold worked, condition suitable for machining; max Brinell may be agreed.
Source: BS 970:1955, Part 2, En 363 (page 206)
Mechanical properties
Condition
Ruling section or size (in)
Tensile strength (tons/sq in)
Yield stress (tons/sq in)
Elongation (%)
Izod impact (ft lb)
Brinell (HB)
Proof stress 0.2% (tons/sq in), when requested
min
-
65
-
-
-
-
-
Values as printed in BS 970:1955; tensile strength, yield stress and proof stress in tons/sq in, Izod in ft lb. Minimum unless a range is shown.
Source: BS 970:1955, Part 2, En 363 (page 207)
Heat treatment
Blank carburise (test bars selected as stated in Clause 7)
880/930 C
Refine (test bars selected as stated in Clause 7)
850/880 C, cool in air or oil
Harden (oil) (test bars selected as stated in Clause 7)
780/820 C
Temperatures in degrees C as printed.
Source: BS 970:1955, Part 2, En 363 (page 207)
Notes
Note
See Appendix A for single quench; by arrangement tests on samples without blank carburising or with short heating.
Source: BS 970:1955, Part 2, En 363
Status in the 1955 edition
Status
Deleted by Amendment 8
Reason
Amendment 8 (Jul 1971): alloy case hardening steels moved to BS 970 Part 3:1971
BS 970:1955 was amended up to Amendment 10 (June 1972); steels were moved to the revised Parts 1 to 5 and deleted from this edition.
Source: BS 970:1955, Amendment slips 6 to 10