BS 970 EN43A vs BS 970 (Part 1) 045A10

Related Material — 69.4% match based on chemical composition and mechanical property overlap.

BS 970 EN43A (BS 970:1955) and BS 970 (Part 1) 045A10 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. BS 970 EN43A is typically used for bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. suitable hardened and tempered for 45/55 (r) and 50/60 (s) tons/sq in according to ruling section; purchaser to state normalised, cold drawn or hardened and tempered r or s. en 43a to 43e., while BS 970 (Part 1) 045A10 is commonly used for case hardening steel (section four). BS 970 EN43A is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 045A10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 EN43A vs BS 970 (Part 1) 045A10 is a 79% match. As per mechanical properties, the match is 50%. Combined, this makes them a related material overall at 69.4%.

Frequently Compared With BS 970 EN43A:
BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 060A40 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 060A45
Match Breakdown
CHEMISTRY MATCH
79%
MECHANICAL MATCH
50%
OVERALL
69.4%
Specifications
Property BS 970 EN43A BS 970 (Part 1) 045A10
Standard BS 970:1955 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.45-0.55 0.08-0.13
Si (%) 0.05-0.35 Not specified
Mn (%) 0.70-1.00 0.30-0.60
S (%) <=0.060 Not specified
P (%) <=0.060 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN43A BS 970 (Part 1) 045A10
Tensile Strength ≥618 MPa (40 tons/sq in, converted) 430 MPa min
Yield Strength ≥324 MPa (21 tons/sq in, converted) Not specified
Elongation ≥18% 18 % min
Hardness 179-229 HB Not specified
Condition Normalised, ruling section 1 1/8 in (lowest-strength condition of the standard) Case hardened, 19 mm test bar
Typical Applications
BS 970 EN43A
Bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. Suitable hardened and tempered for 45/55 (R) and 50/60 (S) tons/sq in according to ruling section; purchaser to state normalised, cold drawn or hardened and tempered R or S. En 43A to 43E.
BS 970 (Part 1) 045A10
Case hardening steel (section four)
Key Differences
Can BS 970 EN43A Be Substituted With BS 970 (Part 1) 045A10?
BS 970 EN43A and BS 970 (Part 1) 045A10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
BS 970 EN43A
0 active listings and RFQs →
BS 970 (Part 1) 045A10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN43A and BS 970 (Part 1) 045A10?
BS 970 EN43A specifies Si, S, P which are not specified for BS 970 (Part 1) 045A10.
Can BS 970 EN43A be substituted with BS 970 (Part 1) 045A10?
BS 970 EN43A and BS 970 (Part 1) 045A10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.