BS 970 (Part 3) 045A10 vs BS 970 (Part 1) 045A10

Strong Match — 94.3% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 045A10 (BS 970 (Part 3):1991) and BS 970 (Part 1) 045A10 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. BS 970 (Part 3) 045A10 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (table 14), while BS 970 (Part 1) 045A10 is commonly used for case hardening steel (section four). BS 970 (Part 3) 045A10 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 045A10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 3) 045A10 vs BS 970 (Part 1) 045A10 is a 94.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.3%.

Frequently Compared With BS 970 (Part 3) 045A10:
BS 970 (Part 1) 060A81 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A67 BS 970 (Part 3) 070M55 BS 970 (Part 1) 060A72 BS 970 (Part 1) 060A78 BS 970 (Part 1) 070A67 BS 970 (Part 1) 045A10 BS 970 (Part 3) 070M20 BS 970 (Part 1) 080A15 BS 970 (Part 3) 080A15 BS 970 (Part 1) 060A47
Match Breakdown
CHEMISTRY MATCH
94.3%
MECHANICAL MATCH
No shared data
OVERALL
94.3%
Specifications
Property BS 970 (Part 3) 045A10 BS 970 (Part 1) 045A10
Standard BS 970 (Part 3):1991 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.08-0.13 0.08-0.13
Si (%) 0.10-0.40 Not specified
Mn (%) 0.30-0.60 0.30-0.60
P (%) <=0.05 Not specified
S (%) <=0.05 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 045A10 BS 970 (Part 1) 045A10
Condition Not specified Case hardened, 19 mm test bar
Tensile Strength Not specified 430 MPa min
Elongation Not specified 18 % min
Typical Applications
BS 970 (Part 3) 045A10
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (Table 14)
BS 970 (Part 1) 045A10
Case hardening steel (section four)
Key Differences
Can BS 970 (Part 3) 045A10 Be Substituted With BS 970 (Part 1) 045A10?
BS 970 (Part 3) 045A10 and BS 970 (Part 1) 045A10 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 045A10 is often considered as a substitute for BS 970 (Part 3) 045A10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 3) 045A10
0 active listings and RFQs →
BS 970 (Part 1) 045A10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 045A10 and BS 970 (Part 1) 045A10?
BS 970 (Part 3) 045A10 specifies Si, P, S which are not specified for BS 970 (Part 1) 045A10.
Can BS 970 (Part 3) 045A10 be substituted with BS 970 (Part 1) 045A10?
BS 970 (Part 3) 045A10 and BS 970 (Part 1) 045A10 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 045A10 is often considered as a substitute for BS 970 (Part 3) 045A10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.