BS 970 (Part 3) 080A15 vs EN 10084 C16R

Strong Match — 92.7% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 080A15 (BS 970 (Part 3):1991) and EN 10084 C16R (EN 10084:2008) are both steel grades. Both fall under the Carbon Steel category. BS 970 (Part 3) 080A15 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; carbon and carbon manganese steel (table 13), while EN 10084 C16R is commonly used for case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1). BS 970 (Part 3) 080A15 is defined under British Standards (BS), originating from United Kingdom, while EN 10084 C16R is defined under European Standard (EN), originating from Europe.

As per chemical composition, BS 970 (Part 3) 080A15 vs EN 10084 C16R is a 92.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.7%.

Frequently Compared With BS 970 (Part 3) 080A15:
BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A62 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 080A15 BS 970 (Part 1) 080A15 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 040A12
Match Breakdown
CHEMISTRY MATCH
92.7%
MECHANICAL MATCH
No shared data
OVERALL
92.7%
Specifications
Property BS 970 (Part 3) 080A15 EN 10084 C16R
Standard BS 970 (Part 3):1991 EN 10084:2008
Category Carbon Steel Carbon Steel
C (%) 0.13-0.18 0.12-0.18
Si (%) 0.10-0.40 <=0.40
Mn (%) 0.70-0.90 0.60-0.90
P (%) <=0.05 <=0.035
S (%) <=0.05 0.020-0.040
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 080A15 EN 10084 C16R
Condition Not specified Soft annealed
Hardness Not specified Soft annealed: 156 HB max
Typical Applications
BS 970 (Part 3) 080A15
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; carbon and carbon manganese steel (Table 13)
EN 10084 C16R
Case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1)
Can BS 970 (Part 3) 080A15 Be Substituted With EN 10084 C16R?
BS 970 (Part 3) 080A15 and EN 10084 C16R overlap closely enough on chemistry and mechanical properties that EN 10084 C16R is often considered as a substitute for BS 970 (Part 3) 080A15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 3) 080A15
0 active listings and RFQs →
EN 10084 C16R
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 080A15 and EN 10084 C16R?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 3) 080A15 be substituted with EN 10084 C16R?
BS 970 (Part 3) 080A15 and EN 10084 C16R overlap closely enough on chemistry and mechanical properties that EN 10084 C16R is often considered as a substitute for BS 970 (Part 3) 080A15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.