BS 970 (Part 3) 080A30 vs BS 970 EN5K

Strong Match — 93.8% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 080A30 (BS 970 (Part 3):1991) and BS 970 EN5K (BS 970:1955) are both steel grades. Both fall under the Carbon Steel category. BS 970 (Part 3) 080A30 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; carbon and carbon manganese steel (table 13), while BS 970 EN5K is commonly used for bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars (excluding cold drawn bars). en 5k is intended for special applications only. same tensile ranges as en 5.. BS 970 (Part 3) 080A30 is defined under British Standards (BS), originating from United Kingdom, while BS 970 EN5K is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 3) 080A30 vs BS 970 EN5K is a 93.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.8%.

Frequently Compared With BS 970 (Part 3) 080A30:
BS 970 (Part 3) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 3) 080A15 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 060A40 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A10
Match Breakdown
CHEMISTRY MATCH
93.8%
MECHANICAL MATCH
No shared data
OVERALL
93.8%
Specifications
Property BS 970 (Part 3) 080A30 BS 970 EN5K
Standard BS 970 (Part 3):1991 BS 970:1955
Category Carbon Steel Carbon Steel
C (%) 0.26-0.34 0.25-0.35
Si (%) 0.10-0.40 0.05-0.35
Mn (%) 0.70-0.90 0.60-1.00
P (%) <=0.05 <=0.050
S (%) <=0.05 <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 080A30 BS 970 EN5K
Tensile Strength Not specified ≥494 MPa (32 tons/sq in, converted)
Yield Strength Not specified ≥247 MPa (16 tons/sq in, converted)
Elongation Not specified ≥25%
Hardness Not specified 143-193 HB
Condition Not specified Normalised, ruling section 2 1/2 in (lowest-strength condition of the standard)
Typical Applications
BS 970 (Part 3) 080A30
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; carbon and carbon manganese steel (Table 13)
BS 970 EN5K
Bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars (excluding cold drawn bars). En 5K is intended for special applications only. Same tensile ranges as En 5.
Can BS 970 (Part 3) 080A30 Be Substituted With BS 970 EN5K?
BS 970 (Part 3) 080A30 and BS 970 EN5K overlap closely enough on chemistry and mechanical properties that BS 970 EN5K is often considered as a substitute for BS 970 (Part 3) 080A30 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 3) 080A30
0 active listings and RFQs →
BS 970 EN5K
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 080A30 and BS 970 EN5K?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 3) 080A30 be substituted with BS 970 EN5K?
BS 970 (Part 3) 080A30 and BS 970 EN5K overlap closely enough on chemistry and mechanical properties that BS 970 EN5K is often considered as a substitute for BS 970 (Part 3) 080A30 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.