BS 970 (Part 3) 080A47 vs NF A35-552 XC48

Strong Match — 91.7% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 080A47 (BS 970 (Part 3):1991) and NF A35-552 XC48 (NF A35-552:1986) are both steel grades. Both fall under the Carbon Steel category. BS 970 (Part 3) 080A47 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; carbon and carbon manganese steel (table 13), while NF A35-552 XC48 is commonly used for used for gears, axles, rollers, machine spindles, hand tools, and wear-resistant parts.. BS 970 (Part 3) 080A47 is defined under British Standards (BS), originating from United Kingdom, while NF A35-552 XC48 is defined under Association Francaise de Normalisation (NF), originating from France.

As per chemical composition, BS 970 (Part 3) 080A47 vs NF A35-552 XC48 is a 91.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91.7%.

Frequently Compared With BS 970 (Part 3) 080A47:
BS 970 (Part 1) 040A12 BS 970 (Part 3) 080A15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 060A62 BS 970 (Part 1) 060A67 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10
Match Breakdown
CHEMISTRY MATCH
91.7%
MECHANICAL MATCH
No shared data
OVERALL
91.7%
Specifications
Property BS 970 (Part 3) 080A47 NF A35-552 XC48
Standard BS 970 (Part 3):1991 NF A35-552:1986
Category Carbon Steel Carbon Steel
C (%) 0.45-0.50 0.45-0.52
Si (%) 0.10-0.40 0.10-0.35
Mn (%) 0.70-0.90 0.50-0.80
P (%) <=0.05 0.045 max
S (%) <=0.05 0.045 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 080A47 NF A35-552 XC48
Tensile Strength Not specified 700-850 MPa
Yield Strength Not specified 400-550 MPa
Elongation Not specified 14-20%
Hardness Not specified 190-255 HB
Typical Applications
BS 970 (Part 3) 080A47
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; carbon and carbon manganese steel (Table 13)
NF A35-552 XC48
Used for gears, axles, rollers, machine spindles, hand tools, and wear-resistant parts.
Can BS 970 (Part 3) 080A47 Be Substituted With NF A35-552 XC48?
BS 970 (Part 3) 080A47 and NF A35-552 XC48 overlap closely enough on chemistry and mechanical properties that NF A35-552 XC48 is often considered as a substitute for BS 970 (Part 3) 080A47 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
BS 970 (Part 3) 080A47
No active listings currently.
NF A35-552 XC48
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 6300–7000 mm (248.03–275.59 in)
On M-EX Right Now
BS 970 (Part 3) 080A47
0 active listings and RFQs →
NF A35-552 XC48
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 080A47 and NF A35-552 XC48?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 3) 080A47 be substituted with NF A35-552 XC48?
BS 970 (Part 3) 080A47 and NF A35-552 XC48 overlap closely enough on chemistry and mechanical properties that NF A35-552 XC48 is often considered as a substitute for BS 970 (Part 3) 080A47 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.