BS 970 (Part 3) 080M50 vs BS 970 (Part 3) 070M55

Strong Match — 92% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 080M50 (BS 970 (Part 3):1991) and BS 970 (Part 3) 070M55 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. BS 970 (Part 3) 080M50 is typically used for used for shafts, rollers, wear-resistant parts, gears, springs, and machine components., while BS 970 (Part 3) 070M55 is commonly used for used for springs, blades, wear plates, hand tools, shafts, and cutting components.. BS 970 (Part 3) 080M50 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 3) 070M55 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 3) 080M50 vs BS 970 (Part 3) 070M55 is a 92% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92%.

Frequently Compared With BS 970 (Part 3) 080M50:
BS 970 (Part 1) 080A20 BS 970 (Part 1) 040A10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
92%
MECHANICAL MATCH
No shared data
OVERALL
92%
Specifications
Property BS 970 (Part 3) 080M50 BS 970 (Part 3) 070M55
Standard BS 970 (Part 3):1991 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) 0.45-0.55 0.50-0.60
Si (%) 0.10-0.40 0.10-0.40
Mn (%) 0.60-1.00 0.50-0.90
P (%) <=0.05 <=0.05
S (%) <=0.05 <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
BS 970 (Part 3) 080M50
Used for shafts, rollers, wear-resistant parts, gears, springs, and machine components.
BS 970 (Part 3) 070M55
Used for springs, blades, wear plates, hand tools, shafts, and cutting components.
Can BS 970 (Part 3) 080M50 Be Substituted With BS 970 (Part 3) 070M55?
BS 970 (Part 3) 080M50 and BS 970 (Part 3) 070M55 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 070M55 is often considered as a substitute for BS 970 (Part 3) 080M50 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
BS 970 (Part 3) 080M50
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5200–5700 mm (204.72–224.41 in)
BS 970 (Part 3) 070M55
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4800–5800 mm (188.98–228.35 in)
On M-EX Right Now
BS 970 (Part 3) 080M50
2 active listings and RFQs →
BS 970 (Part 3) 070M55
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 080M50 and BS 970 (Part 3) 070M55?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 3) 080M50 be substituted with BS 970 (Part 3) 070M55?
BS 970 (Part 3) 080M50 and BS 970 (Part 3) 070M55 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 070M55 is often considered as a substitute for BS 970 (Part 3) 080M50 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.