BS 970 (Part 3) 416S21 vs IS 1570 (Part 7) 12Cr12MoVH

Close Alternative — 74.8% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 416S21 (BS 970 (Part 3):1991) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 3) 416S21 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (table 17), while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. BS 970 (Part 3) 416S21 is defined under British Standards (BS), originating from United Kingdom, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 3) 416S21 vs IS 1570 (Part 7) 12Cr12MoVH is a 74.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 74.8%.

Frequently Compared With BS 970 (Part 3) 416S21:
IS 1570 (Part 7) 12Cr12MoH EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
74.8%
MECHANICAL MATCH
No shared data
OVERALL
74.8%
Specifications
Property BS 970 (Part 3) 416S21 IS 1570 (Part 7) 12Cr12MoVH
Standard BS 970 (Part 3):1991 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.09-0.15 0.08-0.16
Si (%) <=1.0 <=0.60
Mn (%) <=1.5 0.40-1.00
P (%) <=0.060 <=0.040
S (%) 0.15-0.35 <=0.035
Cr (%) 11.5-13.5 11.5-13.00
Mo (%) <=0.60 0.40-0.80
Ni (%) <=1.00 <=1.0
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 416S21 IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength Not specified 770-930 MPa
Yield Strength Not specified >=585 MPa (0.2 % proof stress)
Elongation Not specified >=15%
Condition Not specified Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
BS 970 (Part 3) 416S21
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (Table 17)
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can BS 970 (Part 3) 416S21 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
BS 970 (Part 3) 416S21 and IS 1570 (Part 7) 12Cr12MoVH are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
BS 970 (Part 3) 416S21
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 416S21 and IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 7) 12Cr12MoVH specifies V which is not specified for BS 970 (Part 3) 416S21.
Can BS 970 (Part 3) 416S21 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
BS 970 (Part 3) 416S21 and IS 1570 (Part 7) 12Cr12MoVH are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.