BS 970 (Part 3) 530M40 vs IS 11169 (Part 1) 40Cr4

Strong Match — 95.9% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 530M40 (BS 970 (Part 3):1991) and IS 11169 (Part 1) 40Cr4 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 3) 530M40 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy direct hardening steel (table 16), while IS 11169 (Part 1) 40Cr4 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). BS 970 (Part 3) 530M40 is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 1) 40Cr4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 3) 530M40 vs IS 11169 (Part 1) 40Cr4 is a 95.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95.9%.

Frequently Compared With BS 970 (Part 3) 530M40:
IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 103Cr4 IS 4367 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
95.9%
MECHANICAL MATCH
No shared data
OVERALL
95.9%
Specifications
Property BS 970 (Part 3) 530M40 IS 11169 (Part 1) 40Cr4
Standard BS 970 (Part 3):1991 IS 11169 (Part 1):1984
Category Alloy Steel Alloy Steel
C (%) 0.36-0.44 0.35-0.45
Si (%) 0.10-0.40 0.10-0.35
Mn (%) 0.60-0.90 0.60-0.90
P (%) <=0.035 Not specified
S (%) <=0.040 Not specified
Cr (%) 0.90-1.20 0.90-1.20
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 530M40 IS 11169 (Part 1) 40Cr4
Tensile Strength (hardened and tempered) Not specified 1000-1200 MPa (16 mm) / 900-1180 MPa (40 mm) / 800-950 MPa (100 mm)
0.2% Proof Stress Not specified >=800 MPa (16 mm) / >=680 MPa (40 mm) / >=570 MPa (100 mm)
Elongation Not specified >=11% (16 mm) / >=12% (40 mm) / >=14% (100 mm)
Hardness, annealed Not specified <=200 HB
Typical Applications
BS 970 (Part 3) 530M40
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy direct hardening steel (Table 16)
IS 11169 (Part 1) 40Cr4
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Key Differences
Can BS 970 (Part 3) 530M40 Be Substituted With IS 11169 (Part 1) 40Cr4?
BS 970 (Part 3) 530M40 and IS 11169 (Part 1) 40Cr4 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 40Cr4 is often considered as a substitute for BS 970 (Part 3) 530M40 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 3) 530M40
0 active listings and RFQs →
IS 11169 (Part 1) 40Cr4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 530M40 and IS 11169 (Part 1) 40Cr4?
BS 970 (Part 3) 530M40 specifies P, S which are not specified for IS 11169 (Part 1) 40Cr4.
Can BS 970 (Part 3) 530M40 be substituted with IS 11169 (Part 1) 40Cr4?
BS 970 (Part 3) 530M40 and IS 11169 (Part 1) 40Cr4 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 40Cr4 is often considered as a substitute for BS 970 (Part 3) 530M40 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.