Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy direct hardening steel (Table 16)
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Mo
0.32-0.40
0.10-0.40
1.30-1.70
<=0.035
0.15-0.25
0.22-0.32
More data from BS 970 (Part 3):1991
From the standard
Other composition limits
Steel group
Alloy direct hardening steel (Table 16)
Condition of supply
Bright bars: cold drawn, turned or precision ground, in straight lengths
Maximum unless a range is stated.
Source: BS 970 (Part 3):1991, Table 16
Mechanical properties by heat treatment condition
Condition
Reference symbol
Size (mm)
Tensile strength Rm (MPa)
Yield Re, min (MPa)
Elongation, min (%)
Impact Izod, min (J)
Impact KCV, min (J)
Rp0.2, min (MPa)
Hardness HB
Notes
Hardened and tempered + turned or ground
R
> 13 ≤ 100
700-850
525
15
54
50
510
201-255
Hardened and tempered + turned or ground
S
≥ 6 ≤ 63
775-925
585
13
47
42
570
223-277
Hardened and tempered + turned or ground
T
≥ 6 ≤ 29
850-1000
680
11
40
35
665
248-302
Hardened and tempered + cold drawn or hardened and tempered + cold drawn + ground
R
> 29 ≤ 100
700-850
540
11
47
—
525
201-255
Hardened and tempered + cold drawn or hardened and tempered + cold drawn + ground
S
≥ 6 ≤ 63
775-925
600
10
47
—
585
223-277
Hardened and tempered + cold drawn or hardened and tempered + cold drawn + ground
T
≥ 6 ≤ 29
850-1000
700
8
40
—
680
248-302
Condition letters P to Z are the tensile strength ranges of Table 29. Rp0.2 applies when specifically ordered (note 3). Hardness HB is for guidance only except in the softened condition (note 13). Impact: Izod, or KCV when the standard impact test is not required (option A.3).
Source: BS 970 (Part 3):1991, Table 21
Hardness in the softened condition
Turned, ground or cold drawn and finally softened, max
229 max.
Table 21, finally softened condition.
Source: BS 970 (Part 3):1991, Table 21
Heat treatment temperatures
Hardening temperature
840-870 deg C, oil
Tempering temperature
550-680 deg C
Normalizing, hardening and tempering temperatures as given in Tables 27 and 28 (clause 4.2); Table 22 hardening temperatures for case hardening steels.
Source: BS 970 (Part 3):1991, Table 28