BS 970 (Part 3) 822M17 vs IS 11169 (Part 1) 16Ni8Cr6Mo2

Strong Match — 89.9% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 822M17 (BS 970 (Part 3):1991) and IS 11169 (Part 1) 16Ni8Cr6Mo2 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 3) 822M17 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (table 15), while IS 11169 (Part 1) 16Ni8Cr6Mo2 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b). BS 970 (Part 3) 822M17 is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 1) 16Ni8Cr6Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 3) 822M17 vs IS 11169 (Part 1) 16Ni8Cr6Mo2 is a 89.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.9%.

Frequently Compared With BS 970 (Part 3) 822M17:
IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 4367 07Cr4Mo6 UNI 11234 100Cr6 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
89.9%
MECHANICAL MATCH
No shared data
OVERALL
89.9%
Specifications
Property BS 970 (Part 3) 822M17 IS 11169 (Part 1) 16Ni8Cr6Mo2
Standard BS 970 (Part 3):1991 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.14-0.20 0.12-0.20
Si (%) 0.10-0.40 0.10-0.35
Mn (%) 0.40-0.70 0.40-0.70
Cr (%) 1.30-1.70 1.40-1.70
Mo (%) 0.15-0.25 0.15-0.25
Ni (%) 1.75-2.25 1.80-2.20
P (%) <=0.04 <=0.035
S (%) <=0.05 <=0.035
Cu (%) Not specified <=0.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 822M17 IS 11169 (Part 1) 16Ni8Cr6Mo2
Hardness, annealed (+AC) Not specified <=190 HBW
Typical Applications
BS 970 (Part 3) 822M17
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (Table 15)
IS 11169 (Part 1) 16Ni8Cr6Mo2
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can BS 970 (Part 3) 822M17 Be Substituted With IS 11169 (Part 1) 16Ni8Cr6Mo2?
BS 970 (Part 3) 822M17 and IS 11169 (Part 1) 16Ni8Cr6Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 16Ni8Cr6Mo2 is often considered as a substitute for BS 970 (Part 3) 822M17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 3) 822M17
0 active listings and RFQs →
IS 11169 (Part 1) 16Ni8Cr6Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 822M17 and IS 11169 (Part 1) 16Ni8Cr6Mo2?
IS 11169 (Part 1) 16Ni8Cr6Mo2 specifies Cu which is not specified for BS 970 (Part 3) 822M17.
Can BS 970 (Part 3) 822M17 be substituted with IS 11169 (Part 1) 16Ni8Cr6Mo2?
BS 970 (Part 3) 822M17 and IS 11169 (Part 1) 16Ni8Cr6Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 16Ni8Cr6Mo2 is often considered as a substitute for BS 970 (Part 3) 822M17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.