CSA G40.21 50W vs AS/NZS 3678 Grade 350WR

Related Material — 64.5% match based on chemical composition and mechanical property overlap.

CSA G40.21 50W (CSA G40.21-13 (R2023)) and AS/NZS 3678 Grade 350WR (AS/NZS 3678:2016) are both steel grades. Both fall under the Structural Steel (Corten / Weathering) category. CSA G40.21 50W is typically used for bridges, architectural structures, transmission towers, outdoor exposed structures, railway wagons., while AS/NZS 3678 Grade 350WR is commonly used for weather-resistant (corrosion-resistant) structural steel; exposed bridge and structural applications requiring atmospheric corrosion resistance. CSA G40.21 50W is defined under Canadian Standards Association (CSA), originating from Canada, while AS/NZS 3678 Grade 350WR is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, CSA G40.21 50W vs AS/NZS 3678 Grade 350WR is a 85.3% match. As per mechanical properties, the match is 22.8%. Combined, this makes them a related material overall at 64.5%.

Frequently Compared With CSA G40.21 50W:
CSA G40.21 260WT CSA G40.21 350A ASTM A588 Grade A EN 10025-5 S355J2W EN 10025-5 S355J0WP ASTM A588 EN 10025-5 S355J2WP ASTM A709 Grade HPS 70W CSA G40.21 480A JIS G3114 SMA400 ASTM A588 Grade B EN 10025-5 S235J2W
Match Breakdown
CHEMISTRY MATCH
85.3%
MECHANICAL MATCH
22.8%
OVERALL
64.5%
Specifications
Property CSA G40.21 50W AS/NZS 3678 Grade 350WR
Standard CSA G40.21-13 (R2023) AS/NZS 3678:2016
Category Structural Steel (Corten / Weathering) Structural Steel (Corten / Weathering)
C (%) max 0.19 <=0.20
Mn (%) max 1.35 <=1.70
Si (%) max 0.65 <=0.50
P (%) max 0.035 <=0.035
S (%) max 0.035 <=0.035
Cu (%) 0.25-0.4 0.25-0.55
Cr (%) 0.4-0.65 0.40-0.80
Ni (%) 0.4-0.7 <=0.65
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property CSA G40.21 50W AS/NZS 3678 Grade 350WR
Yield Strength 345 MPa (50 ksi) min 350 MPa min
Tensile Strength 450-655 MPa (65-95 ksi) 480-620 MPa
Elongation 19% min 20% min
Typical Applications
CSA G40.21 50W
Bridges, architectural structures, transmission towers, outdoor exposed structures, railway wagons.
AS/NZS 3678 Grade 350WR
Weather-resistant (corrosion-resistant) structural steel; exposed bridge and structural applications requiring atmospheric corrosion resistance
Can CSA G40.21 50W Be Substituted With AS/NZS 3678 Grade 350WR?
CSA G40.21 50W and AS/NZS 3678 Grade 350WR share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
CSA G40.21 50W
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2700–4300 mm (106.3–169.29 in)
AS/NZS 3678 Grade 350WR
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–2800 mm (98.43–110.24 in)
On M-EX Right Now
CSA G40.21 50W
2 active listings and RFQs →
AS/NZS 3678 Grade 350WR
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between CSA G40.21 50W and AS/NZS 3678 Grade 350WR?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can CSA G40.21 50W be substituted with AS/NZS 3678 Grade 350WR?
CSA G40.21 50W and AS/NZS 3678 Grade 350WR share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.