DIN 17210 15CrMo5 vs UNI 11234 100Cr6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

DIN 17210 15CrMo5 (DIN 17210:1986) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades. Both fall under the Alloy Steel category. DIN 17210 15CrMo5 is typically used for used in gears, pinions, camshafts, transmission shafts, and wear-resistant machine parts., while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components. DIN 17210 15CrMo5 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.

As per chemical composition, DIN 17210 15CrMo5 vs UNI 11234 100Cr6 is a 66.9% match. As per mechanical properties, the match is 27.5%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With DIN 17210 15CrMo5:
NF A35-565 100C6 GOST 4543 12HN3A GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
66.9%
MECHANICAL MATCH
27.5%
OVERALL
35%
Specifications
Property DIN 17210 15CrMo5 UNI 11234 100Cr6
Standard DIN 17210:1986 UNI 11234:2007
Category Alloy Steel Alloy Steel
C (%) 0.13-0.17 0.93-1.05
Si (%) 0.15-0.35 0.15-0.35
Mn (%) 0.80-1.10 0.25-0.45
Cr (%) 1.00-1.30 1.35-1.65
Mo (%) 0.20-0.30 Not specified
P (%) <=0.035 <=0.025
S (%) <=0.035 <=0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property DIN 17210 15CrMo5 UNI 11234 100Cr6
Tensile Strength 700-900 MPa 750-1000 MPa
Yield Strength 500 MPa min 400-600 MPa
Elongation 11-15% 10-14 %
Hardness 220-280 HB 60-64 HRC
Typical Applications
DIN 17210 15CrMo5
Used in gears, pinions, camshafts, transmission shafts, and wear-resistant machine parts.
UNI 11234 100Cr6
ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components
Key Differences
Can DIN 17210 15CrMo5 Be Substituted With UNI 11234 100Cr6?
DIN 17210 15CrMo5 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
DIN 17210 15CrMo5
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5400–7000 mm (212.6–275.59 in)
UNI 11234 100Cr6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6800 mm (224.41–267.72 in)
On M-EX Right Now
DIN 17210 15CrMo5
2 active listings and RFQs →
UNI 11234 100Cr6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between DIN 17210 15CrMo5 and UNI 11234 100Cr6?
DIN 17210 15CrMo5 specifies Mo which is not specified for UNI 11234 100Cr6.
Can DIN 17210 15CrMo5 be substituted with UNI 11234 100Cr6?
DIN 17210 15CrMo5 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.