DIN 17211 41CrAlMo7-4 vs BS 970 (Part 1) 708H45

Close Alternative — 72.3% match based on chemical composition and mechanical property overlap.

DIN 17211 41CrAlMo7-4 (DIN 17211:1987) and BS 970 (Part 1) 708H45 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. DIN 17211 41CrAlMo7-4 is typically used for used for nitrided shafts, gears, crankshafts, spindles, extrusion screws, and wear-resistant machine components., while BS 970 (Part 1) 708H45 is commonly used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6.. DIN 17211 41CrAlMo7-4 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while BS 970 (Part 1) 708H45 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, DIN 17211 41CrAlMo7-4 vs BS 970 (Part 1) 708H45 is a 72.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 72.3%.

Frequently Compared With DIN 17211 41CrAlMo7-4:
NF A35-565 100C6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
72.3%
MECHANICAL MATCH
No shared data
OVERALL
72.3%
Specifications
Property DIN 17211 41CrAlMo7-4 BS 970 (Part 1) 708H45
Standard DIN 17211:1987 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
C (%) 0.38–0.48 0.42-0.49
Mn (%) 0.40–0.70 0.65-1.05
Cr (%) 1.40–1.80 0.80-1.25
Mo (%) 0.20–0.30 0.15-0.25
Al (%) 0.85–1.20 Not specified
P (%) Not specified <=0.035
S (%) Not specified <=0.040
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property DIN 17211 41CrAlMo7-4 BS 970 (Part 1) 708H45
Tensile Strength 900–1050 MPa Not specified
Surface Hardness HV ≥950 (nitrided) Not specified
Typical Applications
DIN 17211 41CrAlMo7-4
Used for nitrided shafts, gears, crankshafts, spindles, extrusion screws, and wear-resistant machine components.
BS 970 (Part 1) 708H45
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Key Differences
Can DIN 17211 41CrAlMo7-4 Be Substituted With BS 970 (Part 1) 708H45?
DIN 17211 41CrAlMo7-4 and BS 970 (Part 1) 708H45 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
DIN 17211 41CrAlMo7-4
Round Bar → (4 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 4800–6900 mm (188.98–271.65 in)
BS 970 (Part 1) 708H45
No active listings currently.
On M-EX Right Now
DIN 17211 41CrAlMo7-4
4 active listings and RFQs →
BS 970 (Part 1) 708H45
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between DIN 17211 41CrAlMo7-4 and BS 970 (Part 1) 708H45?
DIN 17211 41CrAlMo7-4 specifies Al which is not specified for BS 970 (Part 1) 708H45. BS 970 (Part 1) 708H45 specifies P, S which are not specified for DIN 17211 41CrAlMo7-4.
Can DIN 17211 41CrAlMo7-4 be substituted with BS 970 (Part 1) 708H45?
DIN 17211 41CrAlMo7-4 and BS 970 (Part 1) 708H45 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.