DIN 17222 C75 vs BS 970 (Part 3) 070M55

Close Alternative — 84.9% match based on chemical composition and mechanical property overlap.

DIN 17222 C75 (DIN 17222:1979-08) and BS 970 (Part 3) 070M55 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. DIN 17222 C75 is typically used for springs, chisels, punches, cutting tools, hand tools, while BS 970 (Part 3) 070M55 is commonly used for used for springs, blades, wear plates, hand tools, shafts, and cutting components.. DIN 17222 C75 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while BS 970 (Part 3) 070M55 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, DIN 17222 C75 vs BS 970 (Part 3) 070M55 is a 88.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.9%.

Frequently Compared With DIN 17222 C75:
BS 970 (Part 1) 040A10 BS 970 (Part 1) 080A20 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
88.1%
MECHANICAL MATCH
No shared data
OVERALL
84.9%
Specifications
Property DIN 17222 C75 BS 970 (Part 3) 070M55
Standard DIN 17222:1979-08 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) 0.70–0.80 0.50-0.60
Si (%) 0.15–0.35 0.10-0.40
Mn (%) 0.50–0.80 0.50-0.90
S (%) ≤0.040 <=0.05
P (%) ≤0.040 <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property DIN 17222 C75 BS 970 (Part 3) 070M55
Tensile Strength 850–1000 MPa (annealed) Not specified
Hardness HRC 58–63 (hardened) Not specified
Hardness HB 229–285 (annealed) Not specified
Typical Applications
DIN 17222 C75
Springs, chisels, punches, cutting tools, hand tools
BS 970 (Part 3) 070M55
Used for springs, blades, wear plates, hand tools, shafts, and cutting components.
Can DIN 17222 C75 Be Substituted With BS 970 (Part 3) 070M55?
DIN 17222 C75 and BS 970 (Part 3) 070M55 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
DIN 17222 C75
Round Bar → (3 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5200–7000 mm (204.72–275.59 in)
BS 970 (Part 3) 070M55
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4800–5800 mm (188.98–228.35 in)
On M-EX Right Now
DIN 17222 C75
3 active listings and RFQs →
BS 970 (Part 3) 070M55
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between DIN 17222 C75 and BS 970 (Part 3) 070M55?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can DIN 17222 C75 be substituted with BS 970 (Part 3) 070M55?
DIN 17222 C75 and BS 970 (Part 3) 070M55 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.