EN 10083-2 C60 vs IS 11169 (Part 1) 40C15

Related Material — 66.1% match based on chemical composition and mechanical property overlap.

EN 10083-2 C60 (EN 10083-2:2006) and IS 11169 (Part 1) 40C15 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Carbon Steel category. EN 10083-2 C60 is typically used for used in springs, knives, wear plates, high-strength wires, and hand tools., while IS 11169 (Part 1) 40C15 is commonly used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c). EN 10083-2 C60 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 1) 40C15 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10083-2 C60 vs IS 11169 (Part 1) 40C15 is a 66.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 66.1%.

Frequently Compared With EN 10083-2 C60:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 3) 045A10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10
Match Breakdown
CHEMISTRY MATCH
66.1%
MECHANICAL MATCH
No shared data
OVERALL
66.1%
Specifications
Property EN 10083-2 C60 IS 11169 (Part 1) 40C15
Standard EN 10083-2:2006 IS 11169 (Part 1):2022
Category Carbon Steel Carbon Steel
C (%) 0.57-0.65 0.36-0.44
Cr (%) <=0.40 <=0.20
Cr+Mo+Ni (%) <=0.63 Not specified
Mn (%) 0.60-0.90 1.35-1.65
Mo (%) <=0.10 <=0.06
Ni (%) <=0.40 <=0.25
P (%) <=0.045 <=0.030
S (%) <=0.045 <=0.050
Si (%) <=0.40 Not specified
Cu (%) Not specified <=0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10083-2 C60 IS 11169 (Part 1) 40C15
Condition Quenched and tempered (+QT), ruling section d <= 16 mm Not specified
Elongation 11% min Not specified
Hardness Soft annealed (+A): 241 HBW max Not specified
Tensile Strength 850 to 1 000 MPa Not specified
Yield Strength 580 MPa min Not specified
Typical Applications
EN 10083-2 C60
Used in springs, knives, wear plates, high-strength wires, and hand tools.
IS 11169 (Part 1) 40C15
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
Key Differences
Can EN 10083-2 C60 Be Substituted With IS 11169 (Part 1) 40C15?
EN 10083-2 C60 and IS 11169 (Part 1) 40C15 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10083-2 C60
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5100–6100 mm (200.79–240.16 in)
IS 11169 (Part 1) 40C15
No active listings currently.
On M-EX Right Now
EN 10083-2 C60
2 active listings and RFQs →
IS 11169 (Part 1) 40C15
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10083-2 C60 and IS 11169 (Part 1) 40C15?
EN 10083-2 C60 specifies Cr+Mo+Ni, Si which are not specified for IS 11169 (Part 1) 40C15. IS 11169 (Part 1) 40C15 specifies Cu which is not specified for EN 10083-2 C60.
Can EN 10083-2 C60 be substituted with IS 11169 (Part 1) 40C15?
EN 10083-2 C60 and IS 11169 (Part 1) 40C15 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.