DIN EN ISO 4957 1.2379 vs IS 1570 (Part 6) 103T3

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

DIN EN ISO 4957 1.2379 (DIN EN ISO 4957:2018-11) and IS 1570 (Part 6) 103T3 (IS 1570 (Part 6):1996) are both steel grades. Both fall under the Tool & Die Steels category. DIN EN ISO 4957 1.2379 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 6) 103T3 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, DIN EN ISO 4957 1.2379 vs IS 1570 (Part 6) 103T3 is a 54.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With DIN EN ISO 4957 1.2379:
EN ISO 683-17 100Cr6 GB/T 1299 4Cr5MoSiV GOST 5950 4H5MFS IS 1570 (Part 6) 133T3 AISI 52100 IS 1570 (Part 6) 55T8 IS 1570 (Part 6) 50T8 IS 1570 (Part 6) 65T6 IS 1570 (Part 6) 75T6 IS 1570 (Part 6) 60T6 IS 1570 (Part 6) 70T3 IS 3748 70T6
Match Breakdown
CHEMISTRY MATCH
54.1%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 103T3
Standard DIN EN ISO 4957:2018-11 IS 1570 (Part 6):1996
Category Tool & Die Steels Tool & Die Steels
C (%) 1.50–1.60 0.95-1.10
Mn (%) 0.25–0.60 <=0.40
Si (%) 0.10–0.40 0.10-0.30
Cr (%) 11.00–13.00 <=0.20
Mo (%) 0.70–1.00 Not specified
V (%) 0.80–1.10 Not specified
S (%) ≤0.030 <=0.035
P (%) ≤0.030 <=0.035
Cu (%) Not specified <=0.25
Ni (%) Not specified <=0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 103T3
Hardness (annealed) ≤255 HB Not specified
Hardness (hardened) 58–62 HRC Not specified
Compressive Strength 2600 MPa Not specified
Typical Applications
DIN EN ISO 4957 1.2379
Blanking dies, forming dies, thread rolling dies, punches, shear blades, gauges, broaches, drawing dies
IS 1570 (Part 6) 103T3
Not documented
Key Differences
Can DIN EN ISO 4957 1.2379 Be Substituted With IS 1570 (Part 6) 103T3?
DIN EN ISO 4957 1.2379 and IS 1570 (Part 6) 103T3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
DIN EN ISO 4957 1.2379
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–3300 mm (110.24–129.92 in)
IS 1570 (Part 6) 103T3
No active listings currently.
On M-EX Right Now
DIN EN ISO 4957 1.2379
2 active listings and RFQs →
IS 1570 (Part 6) 103T3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between DIN EN ISO 4957 1.2379 and IS 1570 (Part 6) 103T3?
DIN EN ISO 4957 1.2379 specifies Mo, V which are not specified for IS 1570 (Part 6) 103T3. IS 1570 (Part 6) 103T3 specifies Cu, Ni which are not specified for DIN EN ISO 4957 1.2379.
Can DIN EN ISO 4957 1.2379 be substituted with IS 1570 (Part 6) 103T3?
DIN EN ISO 4957 1.2379 and IS 1570 (Part 6) 103T3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.