EN 10025-2 S275J0 vs AS/NZS 3679.1 350

Related Material — 62.3% match based on chemical composition and mechanical property overlap.

EN 10025-2 S275J0 (EN 10025-2:2019) and AS/NZS 3679.1 350 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S275J0 is typically used for hot rolled products of structural steels, while AS/NZS 3679.1 350 is commonly used for hot-rolled structural bars and sections for primary structural beams, columns, and framing. EN 10025-2 S275J0 is defined under European Standard (EN), originating from Europe, while AS/NZS 3679.1 350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, EN 10025-2 S275J0 vs AS/NZS 3679.1 350 is a 87.6% match. As per mechanical properties, the match is 11.6%. Combined, this makes them a related material overall at 62.3%.

Frequently Compared With EN 10025-2 S275J0:
ASTM A1008 SS Grade 80 ASTM A572 Gr.65 GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W CSA G40.21 350W CSA G40.21 400A CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 50
Other Structural Steel Grades to Compare With EN 10025-2 S275J0:
ASTM A283C
Match Breakdown
CHEMISTRY MATCH
87.6%
MECHANICAL MATCH
11.6%
OVERALL
62.3%
Specifications
Property EN 10025-2 S275J0 AS/NZS 3679.1 350
Standard EN 10025-2:2019 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) <=0.21 <=0.22
Mn (%) <=1.50 <=1.70
P (%) <=0.030 <=0.040
S (%) <=0.030 <=0.040
N (%) <=0.012 Not specified
Cu (%) <=0.55 Not specified
Si (%) Not specified <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S275J0 AS/NZS 3679.1 350
Tensile Strength 410-560 MPa 480-640 MPa
Yield Strength >=275 MPa 350 MPa min
Elongation >=23% 20% min
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Typical Applications
EN 10025-2 S275J0
Hot rolled products of structural steels
AS/NZS 3679.1 350
Hot-rolled structural bars and sections for primary structural beams, columns, and framing
Key Differences
Can EN 10025-2 S275J0 Be Substituted With AS/NZS 3679.1 350?
EN 10025-2 S275J0 and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-2 S275J0
No active listings currently.
AS/NZS 3679.1 350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3200 mm (114.17–125.98 in)
On M-EX Right Now
EN 10025-2 S275J0
0 active listings and RFQs →
AS/NZS 3679.1 350
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S275J0 and AS/NZS 3679.1 350?
EN 10025-2 S275J0 specifies N, Cu which are not specified for AS/NZS 3679.1 350. AS/NZS 3679.1 350 specifies Si which is not specified for EN 10025-2 S275J0.
Can EN 10025-2 S275J0 be substituted with AS/NZS 3679.1 350?
EN 10025-2 S275J0 and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.