Close Alternative — 80.2% match
based on chemical composition and mechanical property overlap.
EN 10025-2 S460J2 (EN 10025-2:2019) and EN 10025-3 S420JR (EN 10025-3:2019) are both steel grades.
Both fall under the Structural Steel category.
EN 10025-2 S460J2 is typically used for hot rolled products of structural steels, while EN 10025-3 S420JR is commonly used for used in bridges, heavy machinery frames, structural beams, offshore structures, and crane components..
EN 10025-2 S460J2 is defined under European Standard (EN), originating from Europe, while EN 10025-3 S420JR is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10025-2 S460J2 vs EN 10025-3 S420JR is a 92.7% match.
As per mechanical properties, the match is 55%.
Combined, this makes them a close alternative overall at 80.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10025-2 S460J2
EN 10025-3 S420JR
Tensile Strength
550-720 MPa
520-680 MPa
Yield Strength
>=460 MPa
420 MPa min
Elongation
>=17%
17% min
Condition
Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Not specified
Hardness
Not specified
170-220 HB
Typical Applications
EN 10025-2 S460J2
Hot rolled products of structural steels
EN 10025-3 S420JR
Used in bridges, heavy machinery frames, structural beams, offshore structures, and crane components.
Key Differences
EN 10025-2 S460J2 specifies Cu, Nb, V, Ti which are not specified for EN 10025-3 S420JR.
Can EN 10025-2 S460J2 Be Substituted With EN 10025-3 S420JR?
EN 10025-2 S460J2 and EN 10025-3 S420JR are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10025-2 S460J2 and EN 10025-3 S420JR?
EN 10025-2 S460J2 specifies Cu, Nb, V, Ti which are not specified for EN 10025-3 S420JR.
Can EN 10025-2 S460J2 be substituted with EN 10025-3 S420JR?
EN 10025-2 S460J2 and EN 10025-3 S420JR are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.