Strong Match — 99.5% match
based on chemical composition and mechanical property overlap.
EN 10025-2 S355JR (EN 10025-2:2019) and EN 10025-2 S355J0 (EN 10025-2:2019) are both steel grades.
Both fall under the Structural Steel category.
EN 10025-2 S355JR is typically used for heavy structural work, pressure vessels, offshore structures, while EN 10025-2 S355J0 is commonly used for hot rolled products of structural steels.
EN 10025-2 S355JR is defined under European Standard (EN), originating from Europe, while EN 10025-2 S355J0 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10025-2 S355JR vs EN 10025-2 S355J0 is a 99.2% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 99.5%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10025-2 S355JR
EN 10025-2 S355J0
Tensile Strength
470-630 MPa
470-630 MPa
Yield Strength
>=355 MPa
>=355 MPa
Elongation
>=22%
>=22%
Condition
Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Typical Applications
EN 10025-2 S355JR
Heavy structural work, pressure vessels, offshore structures
EN 10025-2 S355J0
Hot rolled products of structural steels
Can EN 10025-2 S355JR Be Substituted With EN 10025-2 S355J0?
EN 10025-2 S355JR and EN 10025-2 S355J0 overlap closely enough on chemistry and mechanical properties that EN 10025-2 S355J0 is often considered as a substitute for EN 10025-2 S355JR in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10025-2 S355JR and EN 10025-2 S355J0?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10025-2 S355JR be substituted with EN 10025-2 S355J0?
EN 10025-2 S355JR and EN 10025-2 S355J0 overlap closely enough on chemistry and mechanical properties that EN 10025-2 S355J0 is often considered as a substitute for EN 10025-2 S355JR in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.