EN 10025-5 S355J4W vs EN 10025-5 S235J0W

Related Material — 61% match based on chemical composition and mechanical property overlap.

EN 10025-5 S355J4W (EN 10025-5:2019) and EN 10025-5 S235J0W (EN 10025-5:2019) are both steel grades. Both fall under the Structural Steel (Corten / Weathering) category. EN 10025-5 S355J4W is defined under European Standard (EN), originating from Europe, while EN 10025-5 S235J0W is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10025-5 S355J4W vs EN 10025-5 S235J0W is a 89.1% match. As per mechanical properties, the match is 4.9%. Combined, this makes them a related material overall at 61%.

Frequently Compared With EN 10025-5 S355J4W:
EN 10025-5 S235J2W EN 10025-5 S355J0W EN 10025-5 S355J2WP CSA G40.21 480A ASTM A588 Grade A EN 10025-5 S355J2W EN 10025-5 S355J5W EN 10025-5 S355K2W EN 10025-5 S420J5W CSA G40.21 350A ASTM A588 Grade B ASTM A709 Grade HPS 70W
Match Breakdown
CHEMISTRY MATCH
89.1%
MECHANICAL MATCH
4.9%
OVERALL
61%
Specifications
Property EN 10025-5 S355J4W EN 10025-5 S235J0W
Standard EN 10025-5:2019 EN 10025-5:2019
Category Structural Steel (Corten / Weathering) Structural Steel (Corten / Weathering)
C (%) <=0.16 <=0.13
Si (%) <=0.50 <=0.40
Mn (%) 0.50-1.50 0.20-0.60
P (%) <=0.030 <=0.035
S (%) <=0.025 <=0.035
Cr (%) 0.40-0.80 0.40-0.80
Cu (%) 0.25-0.55 0.25-0.55
N (%) Not specified <=0.012
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-5 S355J4W EN 10025-5 S235J0W
Tensile Strength 470-630 MPa 360-510 MPa
Yield Strength >=355 MPa >=235 MPa
Elongation >=22% >=26%
Condition Nominal thickness up to 16 mm for yield, 3 to 100 mm for tensile, 3 to 40 mm for elongation (Lo = 5.65 sqrt(S0), longitudinal); transverse values are lower, see blocks Nominal thickness up to 16 mm for yield, 3 to 100 mm for tensile, 3 to 40 mm for elongation (Lo = 5.65 sqrt(S0), longitudinal); transverse values are lower, see blocks
Key Differences
Can EN 10025-5 S355J4W Be Substituted With EN 10025-5 S235J0W?
EN 10025-5 S355J4W and EN 10025-5 S235J0W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10025-5 S355J4W
0 active listings and RFQs →
EN 10025-5 S235J0W
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-5 S355J4W and EN 10025-5 S235J0W?
EN 10025-5 S235J0W specifies N which is not specified for EN 10025-5 S355J4W.
Can EN 10025-5 S355J4W be substituted with EN 10025-5 S235J0W?
EN 10025-5 S355J4W and EN 10025-5 S235J0W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.