EN 10025-5 S355K2W vs EN 10025-5 S355J0W

Strong Match — 97.9% match based on chemical composition and mechanical property overlap.

EN 10025-5 S355K2W (EN 10025-5:2019) and EN 10025-5 S355J0W (EN 10025-5:2019) are both steel grades. Both fall under the Structural Steel (Corten / Weathering) category. EN 10025-5 S355K2W is defined under European Standard (EN), originating from Europe, while EN 10025-5 S355J0W is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10025-5 S355K2W vs EN 10025-5 S355J0W is a 96.9% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 97.9%.

Frequently Compared With EN 10025-5 S355K2W:
EN 10025-5 S355J2WP EN 10025-5 S355J5W EN 10025-5 S420J2W EN 10025-5 S420K2W EN 10025-5 S355J2W ASTM A588 ASTM A709 Grade HPS 70W AS/NZS 3678 Grade 350WR EN 10025-5 S235J0W EN 10025-5 S235J2W EN 10025-5 S355J0WP EN 10025-5 S355J4W
Match Breakdown
CHEMISTRY MATCH
96.9%
MECHANICAL MATCH
100%
OVERALL
97.9%
Specifications
Property EN 10025-5 S355K2W EN 10025-5 S355J0W
Standard EN 10025-5:2019 EN 10025-5:2019
Category Structural Steel (Corten / Weathering) Structural Steel (Corten / Weathering)
C (%) <=0.16 <=0.16
Si (%) <=0.50 <=0.50
Mn (%) 0.50-1.50 0.50-1.50
P (%) <=0.030 <=0.035
S (%) <=0.030 <=0.035
Cr (%) 0.40-0.80 0.40-0.80
Cu (%) 0.25-0.55 0.25-0.55
N (%) Not specified <=0.012
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-5 S355K2W EN 10025-5 S355J0W
Tensile Strength 470-630 MPa 470-630 MPa
Yield Strength >=355 MPa >=355 MPa
Elongation >=22% >=22%
Condition Nominal thickness up to 16 mm for yield, 3 to 100 mm for tensile, 3 to 40 mm for elongation (Lo = 5.65 sqrt(S0), longitudinal); transverse values are lower, see blocks Nominal thickness up to 16 mm for yield, 3 to 100 mm for tensile, 3 to 40 mm for elongation (Lo = 5.65 sqrt(S0), longitudinal); transverse values are lower, see blocks
Key Differences
Can EN 10025-5 S355K2W Be Substituted With EN 10025-5 S355J0W?
EN 10025-5 S355K2W and EN 10025-5 S355J0W overlap closely enough on chemistry and mechanical properties that EN 10025-5 S355J0W is often considered as a substitute for EN 10025-5 S355K2W in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10025-5 S355K2W
0 active listings and RFQs →
EN 10025-5 S355J0W
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-5 S355K2W and EN 10025-5 S355J0W?
EN 10025-5 S355J0W specifies N which is not specified for EN 10025-5 S355K2W.
Can EN 10025-5 S355K2W be substituted with EN 10025-5 S355J0W?
EN 10025-5 S355K2W and EN 10025-5 S355J0W overlap closely enough on chemistry and mechanical properties that EN 10025-5 S355J0W is often considered as a substitute for EN 10025-5 S355K2W in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.