EN 10028-2 10CrMo9-10 vs IS 1570 (Part 7) 10Cr36Mo10H

Minimal Match — 51.2% match based on chemical composition and mechanical property overlap.

EN 10028-2 10CrMo9-10 (EN 10028-2:2017) and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Alloy Steel category. EN 10028-2 10CrMo9-10 is typically used for flat products for pressure purposes, while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. EN 10028-2 10CrMo9-10 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10028-2 10CrMo9-10 vs IS 1570 (Part 7) 10Cr36Mo10H is a 70.7% match. As per mechanical properties, the match is 12.1%. Combined, this makes them a minimal match overall at 51.2%.

Frequently Compared With EN 10028-2 10CrMo9-10:
EN 10028-2 12CrMo9-10 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 105Cr5 IS 4367 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
70.7%
MECHANICAL MATCH
12.1%
OVERALL
51.2%
Specifications
Property EN 10028-2 10CrMo9-10 IS 1570 (Part 7) 10Cr36Mo10H
Standard EN 10028-2:2017 IS 1570 (Part 7):1992
Category Alloy Steel Alloy Steel
C (%) 0.08-0.14 <=0.15
Si (%) <=0.50 0.25-1.0
Mn (%) 0.40-0.80 0.30-0.60
P (%) <=0.020 <=0.040
S (%) <=0.010 <=0.030
N (%) <=0.012 Not specified
Cr (%) 2.00-2.50 8.00-10.00
Cu (%) <=0.30 Not specified
Mo (%) 0.90-1.10 0.90-1.10
Al (metallic) (%) Not specified <=0.02
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10028-2 10CrMo9-10 IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength 480-630 MPa 410-560 MPa
Yield Strength >=310 MPa >=135 MPa (0.2 % proof stress)
Elongation >=18% >=20%
Condition Usual delivery condition normalized and tempered (+NT), nominal thickness up to 16 mm; transverse direction, Yield Strength is ReH, Elongation is A Pipes, A, thickness - (first row of Table 3)
Typical Applications
EN 10028-2 10CrMo9-10
Flat products for pressure purposes
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can EN 10028-2 10CrMo9-10 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
EN 10028-2 10CrMo9-10 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10028-2 10CrMo9-10
0 active listings and RFQs →
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10028-2 10CrMo9-10 and IS 1570 (Part 7) 10Cr36Mo10H?
EN 10028-2 10CrMo9-10 specifies N, Cu which are not specified for IS 1570 (Part 7) 10Cr36Mo10H. IS 1570 (Part 7) 10Cr36Mo10H specifies Al (metallic) which is not specified for EN 10028-2 10CrMo9-10.
Can EN 10028-2 10CrMo9-10 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
EN 10028-2 10CrMo9-10 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.