EN 10028-2 13CrMo4-5 vs IS 4367 07Cr4Mo6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10028-2 13CrMo4-5 (EN 10028-2:2017) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. EN 10028-2 13CrMo4-5 is defined under European Standard (EN), originating from Europe, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10028-2 13CrMo4-5 vs IS 4367 07Cr4Mo6 is a 67.7% match. As per mechanical properties, the match is 48.5%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10028-2 13CrMo4-5:
NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
67.7%
MECHANICAL MATCH
48.5%
OVERALL
35%
Specifications
Property EN 10028-2 13CrMo4-5 IS 4367 07Cr4Mo6
Standard EN 10028-2:2017 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.08-0.18 <=0.12
Si (%) <=0.35 0.15-0.60
Mn (%) 0.40-1.00 0.40-0.70
P (%) <=0.025 <=0.035
S (%) <=0.010 <=0.035
N (%) <=0.012 Not specified
Cr (%) 0.70-1.15 0.70-1.10
Cu (%) <=0.30 Not specified
Mo (%) 0.40-0.60 0.45-0.65
Ni (%) Not specified <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10028-2 13CrMo4-5 IS 4367 07Cr4Mo6
Tensile Strength 450-600 MPa 380-550 MPa
Yield Strength >=300 MPa 225 MPa min
Elongation >=19% >=19%
Condition Usual delivery condition normalized and tempered (+NT), nominal thickness up to 16 mm; transverse direction, Yield Strength is ReH, Elongation is A Normalised and tempered, ruling section up to 40 mm
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Typical Applications
EN 10028-2 13CrMo4-5
Flat products for pressure purposes
IS 4367 07Cr4Mo6
Not documented
Key Differences
Can EN 10028-2 13CrMo4-5 Be Substituted With IS 4367 07Cr4Mo6?
EN 10028-2 13CrMo4-5 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10028-2 13CrMo4-5
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10028-2 13CrMo4-5 and IS 4367 07Cr4Mo6?
EN 10028-2 13CrMo4-5 specifies N, Cu which are not specified for IS 4367 07Cr4Mo6. IS 4367 07Cr4Mo6 specifies Ni which is not specified for EN 10028-2 13CrMo4-5.
Can EN 10028-2 13CrMo4-5 be substituted with IS 4367 07Cr4Mo6?
EN 10028-2 13CrMo4-5 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.