EN 10028-2 15NiCuMoNb5-6-4 vs IS 4367 07Cr4Mo6

Minimal Match — 34.7% match based on chemical composition and mechanical property overlap.

EN 10028-2 15NiCuMoNb5-6-4 (EN 10028-2:2017) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. EN 10028-2 15NiCuMoNb5-6-4 is defined under European Standard (EN), originating from Europe, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10028-2 15NiCuMoNb5-6-4 vs IS 4367 07Cr4Mo6 is a 52% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 34.7%.

Frequently Compared With EN 10028-2 15NiCuMoNb5-6-4:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 105Cr5
Match Breakdown
CHEMISTRY MATCH
52%
MECHANICAL MATCH
0%
OVERALL
34.7%
Specifications
Property EN 10028-2 15NiCuMoNb5-6-4 IS 4367 07Cr4Mo6
Standard EN 10028-2:2017 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) <=0.17 <=0.12
Si (%) 0.25-0.50 0.15-0.60
Mn (%) 0.80-1.20 0.40-0.70
P (%) <=0.025 <=0.035
S (%) <=0.010 <=0.035
Al (%) >=0.015 Not specified
N (%) <=0.020 Not specified
Cr (%) <=0.30 0.70-1.10
Cu (%) 0.50-0.80 Not specified
Mo (%) 0.25-0.50 0.45-0.65
Nb (%) 0.015-0.045 Not specified
Ni (%) 1.00-1.30 <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10028-2 15NiCuMoNb5-6-4 IS 4367 07Cr4Mo6
Tensile Strength 610-780 MPa 380-550 MPa
Yield Strength >=460 MPa 225 MPa min
Elongation >=16% >=19%
Condition Usual delivery condition normalized and tempered (+NT), nominal thickness up to 40 mm; transverse direction, Yield Strength is ReH, Elongation is A Normalised and tempered, ruling section up to 40 mm
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Typical Applications
EN 10028-2 15NiCuMoNb5-6-4
Flat products for pressure purposes
IS 4367 07Cr4Mo6
Not documented
Key Differences
Can EN 10028-2 15NiCuMoNb5-6-4 Be Substituted With IS 4367 07Cr4Mo6?
EN 10028-2 15NiCuMoNb5-6-4 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10028-2 15NiCuMoNb5-6-4
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10028-2 15NiCuMoNb5-6-4 and IS 4367 07Cr4Mo6?
EN 10028-2 15NiCuMoNb5-6-4 specifies Al, N, Cu, Nb which are not specified for IS 4367 07Cr4Mo6.
Can EN 10028-2 15NiCuMoNb5-6-4 be substituted with IS 4367 07Cr4Mo6?
EN 10028-2 15NiCuMoNb5-6-4 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.