EN 10028-2 P295GH vs EN 10028-2 P235GH

Related Material — 61.2% match based on chemical composition and mechanical property overlap.

EN 10028-2 P295GH (EN 10028-2:2017) and EN 10028-2 P235GH (EN 10028-2:2017) are both steel grades. Both fall under the Carbon Steel category. EN 10028-2 P295GH is typically used for flat products for pressure purposes, while EN 10028-2 P235GH is commonly used for flat products for pressure purposes. EN 10028-2 P295GH is defined under European Standard (EN), originating from Europe, while EN 10028-2 P235GH is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10028-2 P295GH vs EN 10028-2 P235GH is a 90.3% match. As per mechanical properties, the match is 3%. Combined, this makes them a related material overall at 61.2%.

Frequently Compared With EN 10028-2 P295GH:
BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 060A40 BS 970 (Part 1) 060A45 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
90.3%
MECHANICAL MATCH
3%
OVERALL
61.2%
Specifications
Property EN 10028-2 P295GH EN 10028-2 P235GH
Standard EN 10028-2:2017 EN 10028-2:2017
Category Carbon Steel Carbon Steel
C (%) 0.08-0.20 <=0.16
Si (%) <=0.40 <=0.35
Mn (%) 0.90-1.50 0.60-1.20
P (%) <=0.025 <=0.025
S (%) <=0.010 <=0.010
Nb (%) <=0.030 <=0.030
Al (%) >=0.020 >=0.020
N (%) <=0.012 <=0.012
Cr (%) <=0.30 <=0.30
Cu (%) <=0.30 <=0.30
Mo (%) <=0.08 <=0.08
Ni (%) <=0.30 <=0.30
Ti (%) <=0.03 <=0.03
V (%) <=0.02 <=0.02
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10028-2 P295GH EN 10028-2 P235GH
Tensile Strength 460-580 MPa 360-480 MPa
Yield Strength >=295 MPa >=235 MPa
Elongation >=21% >=24%
Condition Usual delivery condition normalized (+N), nominal thickness up to 16 mm; transverse direction, Yield Strength is ReH, Elongation is A Usual delivery condition normalized (+N), nominal thickness up to 16 mm; transverse direction, Yield Strength is ReH, Elongation is A
Typical Applications
EN 10028-2 P295GH
Flat products for pressure purposes
EN 10028-2 P235GH
Flat products for pressure purposes
Can EN 10028-2 P295GH Be Substituted With EN 10028-2 P235GH?
EN 10028-2 P295GH and EN 10028-2 P235GH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10028-2 P295GH
0 active listings and RFQs →
EN 10028-2 P235GH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10028-2 P295GH and EN 10028-2 P235GH?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10028-2 P295GH be substituted with EN 10028-2 P235GH?
EN 10028-2 P295GH and EN 10028-2 P235GH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.