EN 10028-2 P355GH vs BS 970 (Part 1) 045M10

Minimal Match — 31.1% match based on chemical composition and mechanical property overlap.

EN 10028-2 P355GH (EN 10028-2:2017) and BS 970 (Part 1) 045M10 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. EN 10028-2 P355GH is typically used for flat products for pressure purposes, while BS 970 (Part 1) 045M10 is commonly used for case hardening steel (section four). EN 10028-2 P355GH is defined under European Standard (EN), originating from Europe, while BS 970 (Part 1) 045M10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, EN 10028-2 P355GH vs BS 970 (Part 1) 045M10 is a 46.7% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 31.1%.

Frequently Compared With EN 10028-2 P355GH:
BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 060A40 BS 970 (Part 1) 060A45
Match Breakdown
CHEMISTRY MATCH
46.7%
MECHANICAL MATCH
0%
OVERALL
31.1%
Specifications
Property EN 10028-2 P355GH BS 970 (Part 1) 045M10
Standard EN 10028-2:2017 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.10-0.22 0.07-0.13
Si (%) <=0.60 Not specified
Mn (%) 1.10-1.70 0.30-0.60
P (%) <=0.025 Not specified
S (%) <=0.010 Not specified
Nb (%) <=0.040 Not specified
Al (%) >=0.020 Not specified
N (%) <=0.012 Not specified
Cr (%) <=0.30 Not specified
Cu (%) <=0.30 Not specified
Mo (%) <=0.08 Not specified
Ni (%) <=0.30 Not specified
Ti (%) <=0.03 Not specified
V (%) <=0.02 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10028-2 P355GH BS 970 (Part 1) 045M10
Tensile Strength 510-650 MPa 430 MPa min
Yield Strength >=355 MPa Not specified
Elongation >=20% 18 % min
Condition Usual delivery condition normalized (+N), nominal thickness up to 16 mm; transverse direction, Yield Strength is ReH, Elongation is A Case hardened, 19 mm test bar
Typical Applications
EN 10028-2 P355GH
Flat products for pressure purposes
BS 970 (Part 1) 045M10
Case hardening steel (section four)
Key Differences
Can EN 10028-2 P355GH Be Substituted With BS 970 (Part 1) 045M10?
EN 10028-2 P355GH and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10028-2 P355GH
0 active listings and RFQs →
BS 970 (Part 1) 045M10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10028-2 P355GH and BS 970 (Part 1) 045M10?
EN 10028-2 P355GH specifies Si, P, S, Nb which are not specified for BS 970 (Part 1) 045M10.
Can EN 10028-2 P355GH be substituted with BS 970 (Part 1) 045M10?
EN 10028-2 P355GH and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.