Minimal Match — 38% match
based on chemical composition and mechanical property overlap.
EN 10028-3 P355N (EN 10028-3:2017) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades.
Both fall under the Alloy Steel category.
EN 10028-3 P355N is defined under European Standard (EN), originating from Europe, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10028-3 P355N vs IS 4367 07Cr4Mo6 is a 53.1% match.
As per mechanical properties, the match is 8%.
Combined, this makes them a minimal match overall at 38%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10028-3 P355N
IS 4367 07Cr4Mo6
Tensile Strength
490-630 MPa
380-550 MPa
Yield Strength
>=355 MPa
225 MPa min
Elongation
>=22%
>=19%
Condition
Normalized, nominal thickness up to 16 mm
Normalised and tempered, ruling section up to 40 mm
Izod Impact
Not specified
60 J min
Hardness (soft annealed)
Not specified
<=170 HB
Typical Applications
EN 10028-3 P355N
Flat products for pressure equipment
IS 4367 07Cr4Mo6
Not documented
Key Differences
EN 10028-3 P355N specifies Al, N, Cu, Nb which are not specified for IS 4367 07Cr4Mo6.
Can EN 10028-3 P355N Be Substituted With IS 4367 07Cr4Mo6?
EN 10028-3 P355N and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10028-3 P355N and IS 4367 07Cr4Mo6?
EN 10028-3 P355N specifies Al, N, Cu, Nb which are not specified for IS 4367 07Cr4Mo6.
Can EN 10028-3 P355N be substituted with IS 4367 07Cr4Mo6?
EN 10028-3 P355N and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.