EN 10083-1:1991 2C22: A low carbon special steel for quenching and tempering to EN 10083-1:1991 (printed 2 C 22), with sulphur max. 0.035%. Supplied as semi-finished products, bars, rod, wide flats, hot rolled strip, sheet and plate, and forgings. Quenched and tempered tensile strength 500 to 650 MPa for ruling sections up to 16 mm.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Cr
Cr+Mo+Ni
Mn
Mo
Ni
P
S
Si
0.17-0.24
<=0.40
<=0.63
0.40-0.70
<=0.10
<=0.40
<=0.035
<=0.035
<=0.40
Mechanical Properties
Condition
Quenched and tempered, ruling section d <= 16 mm
Elongation
20% min
Tensile Strength
500 to 650 MPa
Yield Strength
340 MPa min
More data from EN 10083-1:1991
From the standard
Other composition limitsTable III and its notes
Designation as printed
2 C 22
Pair grade
3C22 has the same limits except sulphur, controlled 0.020 to 0.040
Improved machinability
Steels with lead or higher sulphur, up to about 0.100% S, may be supplied on request (Table III, note 3)
Restricted options
Without hardenability or quenched and tempered or normalized property requirements, a carbon range of 0.05 and/or Cr + Mo + Ni below 0.45 may be agreed (Table III, note 5)
Elements not quoted in Table III are not intentionally added without the purchaser's agreement, other than for finishing the heat. With hardenability requirements, slight deviations within Table IV are permitted except for carbon, phosphorus and sulphur.
Source: EN 10083-1:1991 (UNI EN 10083-1), Table III and its notes
Mechanical properties, quenched and tempered2 sections
Ruling section
Yield strength Re, min (MPa)
Tensile strength Rm (MPa)
Elongation A, min (%)
Reduction of area Z, min (%)
Impact KV, min (J)
d <= 16 mm, t <= 8 mm
340
500 to 650
20
50
50
16 mm < d <= 40 mm, 8 mm < t <= 20 mm
290
470 to 620
22
50
50
Re is the upper yield strength or, if no yield phenomenon occurs, the 0.2% proof strength; A on gauge length 5.65 times the root of the original cross section; KV on longitudinal ISO V-notch test pieces, average of 3 values, no single value below 70% of the minimum. Ruling sections as in Appendix B. Sizes not listed are not covered by the standard.
Source: EN 10083-1:1991 (UNI EN 10083-1), Table IX
Mechanical properties, normalized2 sizes
Size
Yield strength Re, min (MPa)
Tensile strength Rm, min (MPa)
Elongation A, min (%)
d <= 16 mm, t <= 16 mm
240
430
24
16 mm < d <= 100 mm, 16 mm < t <= 100 mm
210
410
25
Values also apply to the grades with hardenability requirements (H, HH, HL). Sizes not listed are not covered by the standard.
Source: EN 10083-1:1991 (UNI EN 10083-1), Table X
Maximum hardness by delivery conditionTable VIII
Shearability
Shearable in the untreated condition under suitable conditions (clause 5.3.2.3)
Values also apply to the grades with hardenability requirements (H, HH, HL); not applicable to continuously cast slabs not further deformed.
Source: EN 10083-1:1991 (UNI EN 10083-1), Table VIII
Heat treatmentTable XIII
Quenching
860 to 900 deg C
Quenching agent
Water
Tempering
550 to 660 deg C
Normalizing
880 to 920 deg C
Guidance values except the end quench test temperature, which is binding. Lower quenching temperatures generally for water, upper for oil; austenitizing at least 30 min, tempering at least 60 min (guide values).
Source: EN 10083-1:1991 (UNI EN 10083-1), Table XIII