Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10083-1 37Cr4 (EN 10083-1:1991) and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Alloy Steel category.
EN 10083-1 37Cr4 is typically used for quenched and tempered machine parts; non alloy steels also normalized (clause 1), while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
EN 10083-1 37Cr4 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10083-1 37Cr4 vs IS 1570 (Part 7) 10Cr36Mo10H is a 62.9% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-1 37Cr4
IS 1570 (Part 7) 10Cr36Mo10H
Condition
Quenched and tempered, ruling section d <= 16 mm
Pipes, A, thickness - (first row of Table 3)
Elongation
11% min
>=20%
Hardness
Soft annealed: 235 HB max
Not specified
Tensile Strength
950 to 1150 MPa
410-560 MPa
Yield Strength
750 MPa min
>=135 MPa (0.2 % proof stress)
Typical Applications
EN 10083-1 37Cr4
Quenched and tempered machine parts; non alloy steels also normalized (clause 1)
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
IS 1570 (Part 7) 10Cr36Mo10H specifies Mo, Al (metallic) which are not specified for EN 10083-1 37Cr4.
Can EN 10083-1 37Cr4 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
EN 10083-1 37Cr4 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10083-1 37Cr4 and IS 1570 (Part 7) 10Cr36Mo10H?
IS 1570 (Part 7) 10Cr36Mo10H specifies Mo, Al (metallic) which are not specified for EN 10083-1 37Cr4.
Can EN 10083-1 37Cr4 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
EN 10083-1 37Cr4 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.